牌号 | 焊条对应型号 | 堆焊层硬度 HRC | 特点及主要用途 |
HB-YD172(Q) | D172 | ≥40 | 用于堆焊齿轮、挖泥斗、矿山机械等磨损件。 |
HB-YD207(Q) | D207 | ≥50 | 用于堆焊推土机刀片，螺旋桨等磨损零件。 |
HB-YD212(Q) | D212 | ≥50 | 常温高硬度堆焊，用于堆焊挖斗、矿山机械等受磨损的机件表面。 |
HB-YD256(Q) | D256 | HB≥170 | 高锰钢堆焊，适用于破碎机等受冲击磨损部位的堆焊。 |
HB-YD322(Q) | D322 | ≥55 | 用于堆焊各种冲模及切削刃具，兼用于修复要求耐磨损性能较高之机械零件。 |
HB-YD327A(Q) | ≥55 | 专门用于模具堆焊，耐磨性能高于D322 | |
HB-YD337(Q) | D337 | ≥48 | 用于铸钢或锻钢上堆焊锻模。 |
HB-YD397(Q) | D397 | ≥40 | 用于堆焊铸钢或锻钢做坯体的热锻模或堆焊高强度耐磨件。 |
HB-YD405A(Q) | 52-59 | 用于热轧辊开坯辊堆焊 | |
HB-YD430A(Q) | 20-35 | 用于打底焊 | |
HB-YD488A(Q) | 45-50 | 用于轧辊堆焊 | |
HB-YD507MoA(Q) | 35-45 | 用于阀门堆焊 | |
HB-YD507MoNb(Q) | 33-42 | 用于阀门堆焊 | |
HB-YD518(Q) | 40-50 | 用于连铸辊堆焊 | |
HB-D467Q) | 52-55 | 用于二铁盾构施工刀具刃口堆焊 | |
HB-YD58(Q) | 55-62 | 用于堆焦机磨靴堆焊 | |
HB-YD67(Q) | 58-63 | 用于耐磨表面的堆焊 | |
HB-YD688(Q) | 50-55 | 高铬合金焊丝，用于耐磨打底堆焊 | |
HB-YD888(Q) | 55-63 | 高铬合金焊丝，用于耐磨表面堆焊 | |
HB-YD888Ni(Q) | 55-60 | 高铬合金焊丝，用于耐磨表面堆焊 | |
HB-YD888MoW(Q) | 55-60 | 高铬合金高温耐磨焊丝，耐磨表面堆焊 | |
HB-YD95(Q) | 55-63 | 高铬合金焊丝，用于耐磨表面堆焊 | |
HB-YD988(Q) | 55-63 | 高铬合金焊丝，用于耐磨表面堆焊 | |
HB-YD114(Q) | 50-55 | 高锰钢焊丝，用于受强烈冲击表面堆焊 | |
HB-YD115(Q) | 50-55 | 高锰高铬焊丝，用于受强烈冲击表面堆焊 | |
HB-YD165(Q) | 60-65 | 高硬度耐磨焊丝，适用于磨粒磨损表面堆焊 | |
HB-YD265(Q) | 60-65 | 高硬度耐磨焊丝，适用于磨粒磨损表面堆焊 | |
HB-YD258(Q) | 55-60 | 用于耐磨表面堆焊。 |
S 201 | Sn1 Si0.3Mn0.3 | Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper. | ERCu | |
S 211 | Si3 Mn1 | Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel. | ERCuSi-Al | |
S 212 | Sn5 Cu Rem. | Wear resistance. Argon arc welding of copper alloys and surfacing of steel. | ERCuSn-A | |
S 213 | Sn8 Cu Rem. | Wear resistance. Argon arc welding of copper alloys and surfacing of steel. | ERCuSn-C | |
S 214 | Al7.5 Cu Rem. | Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. | ERCuAl-A1 | |
S 215 | Al9 Cu Rem. | Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. | ERCuAl-A2 | |
S 221 | Cu60 Sn1 Si0.3 | Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. | ||
S 221F | Cu60 Sn1 Si 0.3 | S221 welding rod coated with flux. | ||
S 222 | Cu58Sn0.9Si0.1 | Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. | RBCuZn-C | |
S 222F | Cu58Sn0.9Si0.1 | S222 welding rod coated with flux. | RBCuZn-C | |
S 223 | Cu59 Sn0.6 | Melting point is about 900℃. Braze welding of copper, steel and cast iron. | RBCuZn-A | |
S 224 | Cu62 Si0.5 | Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. | ||
Copper 铜 合 金 | S 225 | Cu48 Ni10 | Melting point is about 935℃and high strength. Braze welding of steel, nickel and carbide alloys. | RBCuZn-D |
S 225F | Cu48 Ni10 | S225 welding rod coated with flux. | RBCuZn-D | |
S 226 | Cu60 Sn0.3 | Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron. | ||
S 227 | Cu58Sn0.9Ni0.5 | Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. | RBCuZn-B | |
S 229 | Cu55 Ni6 Mn4 | Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide. |