MECHANICAL/机械性能

Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min

62

MPa

ASTM D 638

Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min

68

MPa

ASTM D 638

Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min

7

%

ASTM D 638

Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min

130

%

ASTM D 638

Tensile Modulus / 拉伸模量, 50 mm/min

2370

MPa

ASTM D 638

Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span

97

MPa

ASTM D 790

Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span

2340

MPa

ASTM D 790

Hardness，Rockwell / 洛氏硬度 M

70

–

ASTM D 785

Hardness，Rockwell / 洛氏硬度 R

118

–

ASTM D 785

Taber Abrasion / 泰伯磨耗量, CS-17, 1 kg

10

mg/1000cy

ASTM D 1044

Tensile Stress, yield / 抗张程度,屈服, 50 mm/min

63

MPa

ISO 527

Tensile Stress, break / 抗张程度,断裂, 50 mm/min

70

MPa

ISO 527

Tensile Strain, yield / 拉伸伸长,屈服, 50 mm/min

6

%

ISO 527

Tensile Strain, break / 拉伸伸长,断裂, 50 mm/min

110

%

ISO 527

Tensile Modulus / 拉伸模量, 1 mm/min

2350

MPa

ISO 527

Flexural Stress, yield / 弯曲强度,屈服, 2 mm/min

90

MPa

ISO 178

Flexural Modulus / 挠曲模量, 2 mm/min

2300

MPa

ISO 178

IMPACT/冲击性能

Izod Impact, unnotched / 无缺口悬臂梁冲击, 23°C

3204

J/m

ASTM D 4812

Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C

801

J/m

ASTM D 256

Izod Impact, notched / 悬臂梁缺口冲击强度 (natural, tints)

801

J/m

ASTM D 256

Izod Impact, notched / 悬臂梁缺口冲击强度 (colors)

801

J/m

ASTM D 256

Tensile Impact Type / 拉伸冲击值，类型”S”

577

kJ/m²

ASTM D 1822

Falling Dart Impact / 落锤冲击 (D 3029), 23°C

169

J

ASTM D 3029

Instrumented IMPACT Energy @ peak / 仪表控制抗冲击能量 @ 峰值, 23°C

63

J

ASTM D 3763

Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*4 +23°C

NA

kJ/m²

ISO 180/1U

Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*4 -30°C

NA

kJ/m²

ISO 180/1U

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 +23°C

12

kJ/m²

ISO 180/1A

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 -30°C

10

kJ/m²

ISO 180/1A

Charpy Impact, notched /简支梁缺口冲击强度, 23°C

35

kJ/m²

ISO 179/2C

Charpy（简支梁缺口冲击强度） 23°C, Unnotch（无缺口） Edgew 80*10*4 sp=62mm

NA

kJ/m²

ISO 179/1eU

Charpy（简支梁缺口冲击强度） -30°C, Unnotch（无缺口） Edgew 80*10*4 sp=62mm

NA

kJ/m²

ISO 179/1eU

THERMAL/热性能

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

154

°C

ASTM D 1525

HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）

137

°C

ASTM D 648

HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）

132

°C

ASTM D 648

CTE（线形膨胀系数）, -40°C to 95°C, flow（流动）

6.84E-05

1/°C

ASTM E 831

Specific Heat / 比热

1.25

J/g-°C

ASTM C 351

Thermal Conductivity / 导热系数

0.19

W/m-°C

ASTM C 177

Thermal Conductivity / 导热系数

0.2

W/m-°C

ISO 8302

CTE（线形膨胀系数）, 23°C to 80°C, flow（流动）

7.E-05

1/°C

ISO 11359-2

Ball Pressure Test, 125°C +/- 2°C

PASSES

–

IEC 60695-10-2

Vicat Softening Temp, Rate / 维卡软化温度，等级 A/50

153

°C

ISO 306

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

141

°C

ISO 306

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/120

142

°C

ISO 306

HDT（热变形温度）/Be, 0.45MPa Edgew 120*10*4 sp=100mm

136

°C

ISO 75/Be

HDT（热变形温度）/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm

125

°C

ISO 75/Ae

Relative Temp Index, Elec / 相对热指数， 电性能

130

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

130

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

130

°C

UL 746B

PHYSICAL/物理性能

Specific Gravity / 比重

1.2

–

ASTM D 792

Specific Volume / 比容

0.83

cm³/g

ASTM D 792

Density / 密度

1.19

g/cm³

ASTM D 792

Water Absorption / 吸水率, 24 hours

0.15

%

ASTM D 570

Water Absorption，equilibrium / 吸水率，平衡, 23C

0.35

%

ASTM D 570

Water Absorption，equilibrium / 吸水率，平衡, 100°C

0.58

%

ASTM D 570

Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm

0.5 – 0.7

%

SABIC Method

Melt Flow Rate / 熔流率,, 300°C/1.2 kgf

10.5

g/10 min

ASTM D 1238

Melt Volume Rate / 溶化体积流率, MVR at 300°C/1.2 kg

10

cm³/10 min

ISO 1133

OPTICAL/光学性能

Light Transmission / 透光率

88

%

ASTM D 1003

Haze / 雾度

1

%

ASTM D 1003

Refractive Index / 折射指数

1.586

–

ASTM D 542

ELECTRICAL/电气性能

Volume Resistivity / 体积电阻率

>1.E+17

Ohm-cm

ASTM D 257

Dielectric Strength, in air / 介电强度，空气中, 3.2 mm

14.9

kV/mm

ASTM D 149

Relative Permittivity / 相对介电常数, 50/60 Hz

3.17

–

ASTM D 150

Relative Permittivity / 相对介电常数, 1 MHz

2.96

–

ASTM D 150

Dissipation Factor / 耗散因素, 50/60 Hz

0.0009

–

ASTM D 150

Dissipation Factor / 耗散因素, 1 MHz

0.01

–

ASTM D 150

Hot Wire Ignition / 热丝引燃 {PLC)

2

PLC Code

UL 746A

High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}

2

PLC Code

UL 746A

High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}

1

PLC Code

UL 746A

Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}

2

PLC Code

UL 746A

Volume Resistivity / 体积电阻率

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity ROA / 表面电阻率

>1.E+15

Ohm

IEC 60093

Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm

17

kV/mm

IEC 60243-1

Relative Permittivity / 相对介电常数, 50/60 Hz

2.7

–

IEC 60250

Relative Permittivity / 相对介电常数, 1 MHz

2.7

–

IEC 60250

Dissipation Factor / 耗散因素, 50/60 Hz

0.001

–

IEC 60250

Dissipation Factor / 耗散因素, 1 MHz

0.01

–

IEC 60250

FLAME CHARACTERISTICS/火焰特性

UL Recognized, 94HB Flame Class Rating / 阻燃等级 (3)

1.47

mm

UL 94

Oxygen Index / 极限氧指数 (LOI)

25

%

ASTM D 2863

Oxygen Index / 极限氧指数 (LOI)

25

%

ISO 4589

Injection Molding/注塑参数

Drying Temperature / 干燥温度

120

°C

Drying Time / 干燥时间

3 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

48

hrs

Maximum Moisture Content / 最大含湿量

0.02

%

Melt Temperature / 熔体温度

295 – 315

°C

Nozzle Temperature / 注嘴温度

290 – 310

°C

Front – Zone 3 Temperature / 前区3温度

295 – 315

°C

Middle – Zone 2 Temperature / 中区2温度

280 – 305

°C

Rear – Zone 1 Temperature / 后区1温度

270 – 295

°C

Mold Temperature / 模具温度

70 – 95

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

40 – 70

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比

40 – 60

%

Vent Depth / 排气孔深度

0.025 – 0.076

mm