瑞典伊萨FILARC 118高强钢焊条 E11018-M低合金钢焊条

FILARC 118 SMAW
Type Basic E11018-M
Description
All-positional, basic AC/DC electrode with 120%
recovery for welding steels with min. 680 N/mm2
yield strength; e. g. NAXTRA 70, T1, 80 HLES,
HY80 and HY100. Often applied in combination
with FILARC 98, where the latter is used for tack
welding, root-run welding and for welding standing
fillet welds.
Use the shortest possible arc. Weave slowly
when permitted. A slight weave can be used for
standing fillet welds.
DC+. Use DC- for root runs.
Recovery
120%
Welding current
DC+/-, AC OCV 70 V
12346
Classifications
SFA/AWS A5.5 E11018-M
EN 757 E 69 5 Mn2NiMo B 32 H5
Typical all weld metal composition, %
C Si Mn Ni Mo
0.06 0.4 1.6 2.2 0.4
Typical mech. properties all weld metal
Yield stress, MPa <760
Tensile strength, MPa >760
Elongation, % >20
Charpy V
Test temps, °C Impact values, J
-51 >47
Approvals
ABS E11018-M
BV 4Y62H5
DNV 4 Y62H10
MoD (N) Q1N, HY80
LR 4Y62H5
Welding parameters
Diameter,
mm
Length,
mm
Welding
current, A
Arc voltage,
V
N.
Kg weld
metal/kg
electrodes
B.
No. of electrodes/
kg
weld metal
H.
Kg weld
metal/hour
arc time
T.
Burn-off
time, s/
electrode
2.5 350 55-105 25.3 0.61 83.3 0.93 46.6
3.2 350 90-140 22.8 0.56 46.2 1.21 64.3
4.0 450 110-180 22.8 0.61 23.1 1.72 90.0
5.0 450 190-280 24.6 0.63 13.5 2.75​