产品描述
ULTEM PEI 1000物性表
未增强。DTUL（载荷下挠曲温度）：392F (200C) ，264 psi。UL94 V-0/5V额定。In 1000-1000ONLY–USP Class VI, FDA 食物接触用具与tripartite (ISO 10993-1修订版)。
Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. US FDA and EU Food Contact compliant, NSF 51 listing, compliant in natural color. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU1000.
Property/特性
TYPICAL PROPERTIES (1)
MECHANICAL/机械性能
Value/值 Unit/单位 Standard/标准
Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 5 mm/min
110
MPa
ASTM D 638
Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 5 mm/min
7
%
ASTM D 638
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 5 mm/min
60
%
ASTM D 638
Tensile Modulus / 拉伸模量, 5 mm/min
3580
MPa
ASTM D 638
Flexural Stress, yld / 挠曲强度, 屈服 , 2.6 mm/min, 100 mm span
165
MPa
ASTM D 790
Flexural Modulus / 挠曲模量, 2.6 mm/min, 100 mm span
3510
MPa
ASTM D 790
Hardness，Rockwell / 洛氏硬度 M
109
–
ASTM D 785
Taber Abrasion / 泰伯磨耗量, CS-17, 1 kg
10
mg/1000cy
ASTM D 1044
IMPACT/冲击性能
Value/值 Unit/单位 Standard/标准
Izod Impact, unnotched / 无缺口悬臂梁冲击, 23°C
1335
J/m
ASTM D 4812
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
53
J/m
ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm
1335
J/m
ASTM D 256
Gardner（加德纳冲击强度）, 23°C
36
J
ASTM D 3029
THERMAL/热性能
Value/值 Unit/单位 Standard/标准
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
218
°C
ASTM D 1525
HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）
210
°C
ASTM D 648
HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）
201
°C
ASTM D 648
CTE（线形膨胀系数）, -20°C to 150°C, flow（流动）
5.58E-05
1/°C
ASTM E 831
CTE（线形膨胀系数）, -20°C to 150°C, xflow（横向）
5.4E-05
1/°C
ASTM E 831
Thermal Conductivity / 导热系数
0.22
W/m-°C
ASTM C 177
Relative Temp Index, Elec / 相对热指数， 电性能
170
°C
UL 746B
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
170
°C
UL 746B
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
170
°C
UL 746B
PHYSICAL/物理性能
Value/值 Unit/单位 Standard/标准
Specific Gravity / 比重
1.27
–
ASTM D 792
Water Absorption / 吸水率, 24 hours
0.25
%
ASTM D 570
Water Absorption，equilibrium / 吸水率，平衡, 23C
1.25
%
ASTM D 570
Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm
0.5 – 0.7
%
SABIC Method
Melt Flow Rate / 熔流率,, 337°C/6.6 kgf
9
g/10 min
ASTM D 1238
Poisson’s Ratio
0.3
–
ASTM D 638
ELECTRICAL/电气性能
Value/值 Unit/单位 Standard/标准
Volume Resistivity / 体积电阻率
1.E+17
Ohm-cm
ASTM D 257
Dielectric Strength, in air / 介电强度，空气中, 1.6 mm
32.7
kV/mm
ASTM D 149
Dielectric Strength, in oil / 耐电强度，在油中, 1.6 mm
27.9
kV/mm
ASTM D 149
Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm
19.6
kV/mm
ASTM D 149
Relative Permittivity / 相对介电常数, 100 Hz
3.15
–
ASTM D 150
Relative Permittivity / 相对介电常数, 1 kHz
3.15
–
ASTM D 150
Dissipation Factor / 耗散因素, 100 Hz
0.0015
–
ASTM D 150
Dissipation Factor / 耗散因素, 1 kHz
0.0012
–
ASTM D 150
Dissipation Factor / 耗散因素, 2450 MHz
0.0025
–
ASTM D 150
Arc Resistance, Tungsten / 耐电弧性 {PLC}
5
PLC Code
ASTM D 495
Hot Wire Ignition / 热丝引燃 {PLC)
1
PLC Code
UL 746A
High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}
2
PLC Code
UL 746A
High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}
3
PLC Code
UL 746A
Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}
4
PLC Code
UL 746A
FLAME CHARACTERISTICS/火焰特性
Value/值 Unit/单位 Standard/标准
CSA (See File for complete listing)
LS88480
File No.
CSA LISTED
Oxygen Index / 极限氧指数 (LOI)
47
%
ASTM D 2863
NBS Smoke Density / 密度, Flaming, Ds 4 min
0.7
–
ASTM E 662
Source GMD, last updated:02/24/2003
Processing/加工方法
Parameter
Injection Molding/注塑参数
Value/值 Unit/单位
Drying Temperature / 干燥温度
150
°C
Drying Time / 干燥时间
4 – 6
hrs
Drying Time (Cumulative) / 干燥时间（累积的）
24
hrs
Maximum Moisture Content / 最大含湿量
0.02
%
Melt Temperature / 熔体温度
350 – 400
°C
Nozzle Temperature / 注嘴温度
345 – 400
°C
Front – Zone 3 Temperature / 前区3温度
345 – 400
°C
Middle – Zone 2 Temperature / 中区2温度
340 – 400
°C
Rear – Zone 1 Temperature / 后区1温度
330 – 400
°C
Mold Temperature / 模具温度
135 – 165
°C
Back Pressure / 背压
0.3 – 0.7
MPa
Screw Speed / 螺杆速度
40 – 70
rpm
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
40 – 60
%
Vent Depth / 排气孔深度
0.025 – 0.076
mm
Parameter
Extrusion Blow Molding
Value/值 Unit/单位
Drying Temperature / 干燥温度
140 – 150
°C
Drying Time / 干燥时间
4 – 6
hrs
Drying Time (Cumulative) / 干燥时间（累积的）
24
hrs
Maximum Moisture Content / 最大含湿量
0.01 – 0.02
%
Melt Temperature / 熔体温度(Parison)
320 – 355
°C
Barrel – Zone 1 Temperature / 第1气缸区温度
325 – 350
°C
Barrel – Zone 2 Temperature / 第2气缸区温度
330 – 355
°C
Barrel – Zone 3 Temperature / 第3气缸区温度
330 – 355
°C
Barrel – Zone 4 Temperature / 第4气缸区温度
330 – 355
°C
Adapter – Zone 5 Temperature / 接套-区域5 温度
330 – 355
°C
Head – Zone 6 – Top Temperature / 机头-区域6-上部温度
330 – 355
°C
Head – Zone 7 – Bottom Temperature / 机头-区域7-下部温度
330 – 355
°C
Screw Speed / 螺杆速度
10 – 70
rpm
Mold Temperature / 模具温度
65 – 175
°C
Die Temperature / 模具温度
325 – 355
°C
ultem 1000-1000 为美国ge公司专利，广泛应用于lc，mu类型光纤连接器供应各种颜色pei一次性水口;lc光纤连接器专用料。其物理性能与新料接近，是当今微利时代，降低成本的最佳选择；pei具有很强的高温稳定性，既使是非增强型的pei，仍具有很好的韧性和强度。因此利用pei优越的热稳定性可用来制作高温耐热器件。pei还有良好的阻燃性、抗化学反应以及电绝缘特性。玻璃化转化温度很高，达215c。pei还具有很低的收缩率及良好的等方向机械特性。