产品参数性能项目 试验条件[状态] 测试方法 测试数据 数据单位 物理性能 比重 ASTM D792 1.77-1.8 g/cm3 ISO 1183 1770 kg/m3 熔体流动速率 450℃/12.5 kg ASTM D1238 3-8 g/10 min 熔体体积流动速率 230℃/5.0 kg ISO 1133 1.1 cm3/10min 吸水率 23℃, 24 hr ASTM D570 0.03-0.05 % 饱和 ISO 62 0.03 % 平衡 ISO 62 0.015 % 机械性能 硬度计硬度 支撐 D, 23℃ ASTM D2240 70-75 拉伸模量 23℃ ASTM D638 1030-1520 MPa ISO 527-2 830 MPa 抗张强度 屈服, 23℃ ASTM D638 31-41.4 MPa 屈服 ISO 527-2 35 MPa 断裂, 23℃ ASTM D638 27.6-48.3 MPa 伸长率 屈服, 23℃ ASTM D638 5-15 % 屈服 ISO 527-2 10 % 断裂, 23℃ ASTM D638 30-200 % 断裂伸长率 ISO 527-2 2 > 50 % 拉伸蠕变模量 1 hr ISO 899-1 508 MPa 1000 hr ISO 899-1 210 MPa 弯曲模量 23℃ ASTM D790 1030-1240 MPa 弯曲强度 5.0% 应变,23℃ ASTM D790 20.7-34.5 MPa 压缩强度 23℃ ASTM D695 41.4-58.6 MPa 摩擦系数 与钢 - 动态 ASTM D1894 0.19 与钢 - 静态 ASTM D1894 0.26 抗泰伯磨耗 1000 Cycles, 1000 g, CS-17 转轮 6-9 mg 简支梁缺口冲击强度 -30℃ ISO 179/1eA 5 kJ/m2; 23℃ ISO 179/1eA 29 kJ/m2; 简支梁冲击强度 -30℃ ISO 179/1eU 186 kJ/m2; 悬壁梁缺口冲击强度 23℃ ASTM D256 110-430 J/m
热性能热变形温度 0.45 MPa, 未退火 ASTM D648 60-75 ℃ 0.45 MPa ISO 75-2 114 ℃ 1.8 MPa, 未退火 ASTM D648 37.8-55 ℃ 玻璃转化温度 ISO 11357-2 -38 ℃ DMA -40.6 到 -38.3 ℃ 维卡软化点 50℃/h, B (50N) ISO 306 107 ℃ 熔融温度 ASTM D3418 155-160 ℃ ISO 11357-3 158 ℃ 线形膨胀系数 - 流动 ASTM D696 0.00013-0.00019 cm/cm/℃ ISO 11359-2 0.00016 cm/cm/℃ 比热 DSC 1170-1510 J/kg/℃ 导热系数 ASTM C177 0.14-0.18 W/m/K 阻燃等级 UL 94 V-0 燃烧性能 正常厚度 1.6mm 1.60 mm ISO 1210 V-0 一定厚度与小时下的阻燃等级 0.800 mm ISO 1210 V-0 电气性能 表面电阻率 IEC 60093 1.0E+13 ohm 体积电阻率 20℃ ASTM D257 2.0E+14 ohm·cm IEC 60093 2.0E+12 ohm·cm 介电强度 23℃ ASTM D149 51-63 kV/mm IEC 60243-1 21 kV/mm 介电常数 23℃ ASTM D150 3.5-10.2 100 Hz IEC 60250 10.5 1 MHz IEC 60250 6.5 耗散因数 23℃, 100 Hz ASTM D150 0.01-0.22 100 Hz IEC 60250 0.038 1 MHz IEC 60250 0.23 漏电起痕指数 IEC 60112 600 光学性能 折射率 ASTM D542 1.42 其它 极限氧指数 ASTM D2863 75 % ASTM D2863 43 % ISO 4589-2 42 %
公司主营业务如下:
工程塑料 :EAA,EBA,EMA,POM.PC.PA6.PA66.EVA.PVDC,TPE.TPU.TPV.TPEE.POE.CPE
COC.LCP.PPO.PPS.TPX.SPS.K胶,PEI.PES.PSU.PA9T.PEEK.CAP.LCP.PA46.PA12
氟塑料:PFA.PTFE.FEP.PVDF.ETFE.ECTFE.PCTFE.EFEP.氟橡胶
本公司长期代理销售法国阿科玛 PVDF 多种牌号原料
我司产品均可免费提供详细物性表(英文和中文版)、加工参数表、ROHS(SGS)、物质安全表MSDS、UL黄卡及FDA认证等相关资料;可开17%增值税发票;免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料);如需试料、了解产品相关信息及当日报价,敬请来电、来邮及在线咨询,竭诚为您服务!
由于市场行情有波动,详细价格请旺旺或者来电咨询,为此造成的不便,请您谅解。
★★郑重承诺:本公司所售原料全部为原厂原包正牌料、杜绝一切副牌料、水口料以次充好★★★
手机:13113277385 电话:0769-33216171
QQ:2267812420 邮箱:2267812420@qq.com

| Rheological properties | Value | Unit | Test Standard |
| Melt volume-flow rate, MVR | 10 | cm3/10min | ISO 1133 |
| Temperature | 230 | °C | - |
| Load | 5 | kg | - |
| Molding shrinkage, parallel | 2.0 | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 2.0 | % | ISO 294-4, 2577 |
| Mechanical properties | Value | Unit | Test Standard |
| Tensile Modulus | 2500 | MPa | ISO 527-1/-2 |
| Yield stress | 54 | MPa | ISO 527-1/-2 |
| Yield strain | 8 | % | ISO 527-1/-2 |
| Nominal strain at break | 40 | % | ISO 527-1/-2 |
| Charpy impact strength, +23°C | 232 | kJ/m2 | ISO 179/1eU |
| Charpy impact strength, -30°C | 218 | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength, +23°C | 11 | kJ/m2 | ISO 179/1eA |
| Charpy notched impact strength, -30°C | 5 | kJ/m2 | ISO 179/1eA |
| Thermal properties | Value | Unit | Test Standard |
| Melting temperature, 10°C/min | 171 | °C | ISO 11357-1/-3 |
| Glass transition temperature, 10°C/min | -40 | °C | ISO 11357-1/-2 |
| Temp. of deflection under load, 1.80 MPa | 110 | °C | ISO 75-1/-2 |
| Vicat softening temperature, 50°C/h 50N | 141 | °C | ISO 306 |
| Coeff. of linear therm. expansion, parallel | 136 | E-6/K | ISO 11359-1/-2 |
| Burning Behav. at 1.5 mm nom. thickn. | V-0 | class | IEC 60695-11-10 |
| Thickness tested | 1.6 | mm | - |
| Burning Behav. at thickness h | V-0 | class | IEC 60695-11-10 |
| Thickness tested | 0.8 | mm | - |
| Oxygen index | 67 | % | ISO 4589-1/-2 |
| Electrical properties | Value | Unit | Test Standard |
| Relative permittivity, 100Hz | 10 | - | IEC 60250 |
| Relative permittivity, 1MHz | 7.5 | - | IEC 60250 |
| Dissipation factor, 100Hz | 310 | E-4 | IEC 60250 |
| Dissipation factor, 1MHz | 2160 | E-4 | IEC 60250 |
| Other properties | Value | Unit | Test Standard |
| Water absorption | 0.03 | % | Sim. to ISO 62 |
| Humidity absorption | 0.015 | % | Sim. to ISO 62 |
| Density | 1780 | kg/m3 | ISO 1183 |
| Test specimen production | Value | Unit | Test Standard |
| Injection Molding, melt temperature | 210 | °C | ISO 294 |
| Injection Molding, mold temperature | 90 | °C | ISO 10724 |
| Injection Molding, injection velocity | 10 | mm/s | ISO 294 |
| Injection Molding, pressure at hold | 13 | MPa | ISO 294 |