DuPont Zytel® 103FHS NC010 Nylon 66

Physical Properties物理性质

Metric公制数据

English英制数据

Comments测试方法

Specific Gravity比重 

 g/cc

1.14 g/cc

DAM; ASTM D792

Density密度 

1.14 g/cc

0.0412 lb/in³

DAM; ISO 1183

Water Absorption吸水率 

1.2 %
@Temperature 23.0 °C

1.2 %
@Temperature 73.4 °F

Immersion 24h; DAM; ASTM D570

8.5 %
@Temperature 23.0 °C

8.5 %
@Temperature 73.4 °F

Saturation, immersed; DAM; ISO 62, Similar to

8.6 %
@Temperature 23.0 °C

8.6 %
@Temperature 73.4 °F

Saturation; DAM; ASTM D570

Linear Mold Shrinkage线性收缩率 

0.014 cm/cm
@Thickness 1.60 mm

0.014 in/in
@Thickness 0.0630 in

Flow; DAM

0.018 cm/cm
@Thickness 3.20 mm

0.018 in/in
@Thickness 0.126 in

Flow; DAM

Linear Mold Shrinkage, Flow 线性收缩率/流动

0.014 cm/cm
@Thickness 2.00 mm

0.014 in/in
@Thickness 0.0787 in

Parallel; DAM; ISO 294-4

Linear Mold Shrinkage, Transverse线性收缩率/横向 

0.013 cm/cm
@Thickness 2.00 mm

0.013 in/in
@Thickness 0.0787 in

Normal; DAM; ISO 294-4

Mechanical Properties力学性能

Metric公制数据

English英制数据

Comments测试方法

Hardness, Rockwell R罗氏硬度R 

121

121

DAM; ASTM D785

Tensile Strength拉伸强度 

41.0 MPa
@Temperature 121 °C

5950 psi
@Temperature 250 °F

DAM; ASTM D638

83.0 MPa
@Temperature 23.0 °C

12000 psi
@Temperature 73.4 °F

DAM; ASTM D638

Tensile Stress拉伸应力 

0.000 MPa
@Strain 0.000 %,
Temperature -40.0 °C

0.000 psi
@Strain 0.000 %,
Temperature -40.0 °F

DAM; ISO 11403-1/-2

7.03 MPa
@Strain 1.10 %,
Temperature 60.0 °C

1020 psi
@Strain 1.10 %,
Temperature 140 °F

50%RH; ISO 11403-1/-2

25.58 MPa
@Strain 14.0 %,
Temperature 120 °C

3710 psi
@Strain 14.0 %,
Temperature 248 °F

DAM; ISO 11403-1/-2

29.95 MPa
@Strain 21.0 %,
Temperature 100 °C

4344 psi
@Strain 21.0 %,
Temperature 212 °F

50%RH; ISO 11403-1/-2