PBT/台湾长春/3015-201 增强级 耐高温 热稳定性纤维 塑料
物理性能额定值 (公制)额定值 (英制)测试方法
| 比重 | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| 水分吸收 | 0.0400 % @Time 86400 sec | 0.0400 % @Time 24.0 hour | ASTM D570 |
| 线性成型收缩率 | 0.0030 - 0.0060 cm/cm @Thickness 1.60 mm | 0.0030 - 0.0060 in/in @Thickness 0.0630 in | horizontal; ASTM D955 |
| 0.014 - 0.020 cm/cm @Thickness 1.60 mm | 0.014 - 0.020 in/in @Thickness 0.0630 in | vertical; ASTM D955 |
机械性能额定值 (公制)额定值 (英制)测试方法
| 洛氏硬度（M 级） | 90 | 90 | ASTM D785 |
| 抗张强度 | 93.2 MPa | 13500 psi | ASTM D638 |
| 伸长率 (断裂) | 4.0 % | 4.0 % | ASTM D638 |
| 弯曲强度 | 150 MPa | 21800 psi | ASTM D790 |
| 弯曲模量 | 4.90 GPa | 711 ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | >= 0.588 J/cm @Thickness 6.35 mm | >= 1.10 ft-lb/in @Thickness 0.250 in | ASTM D256 |
电气性能额定值 (公制)额定值 (英制)测试方法
| 体积电阻率 | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| 表面电阻 | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 |
| 介电常数 | 3.5 @Frequency 60.0 Hz | 3.5 @Frequency 60.0 Hz | ASTM D150 |
| 介电强度 | 20.0 kV/mm @Thickness 2.00 mm | 508 kV/in @Thickness 0.0787 in | ASTM D149 |
| 耗散因数 | 0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | ASTM D150 |
| 耐电弧性 | 100 sec | 100 sec | ASTM D495 |
热性能额定值 (公制)额定值 (英制)测试方法
| 线性热膨胀系数 | 50.0 µm/m-°C | 27.8 µin/in-°F | ASTM D696 |
| 熔融温度 | 225 °C | 437 °F | DSC |
| 载荷下热变形温度(0.46 MPa) | 220 °C | 428 °F | ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 200 °C | 392 °F | ASTM D648 |
| 可燃性(UL94) | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |
加工性能额定值 (公制)额定值 (英制)测试方法
| 加工温度 | 240 - 270 °C | 464 - 518 °F | |
| 射嘴温度 | 260 - 270 °C | 500 - 518 °F | |
| 模具温度 | 40.0 - 120 °C | 104 - 248 °F | suitable temperature 60-80°C |
| 注射压力 | 50.0 - 120 MPa | 7250 - 17400 psi | |
| 保压 | 30.0 - 80.0 MPa | 4350 - 11600 psi | |
| 背压 | 0.000 - 0.300 MPa | 0.000 - 43.5 psi | |
| 螺杆转速 | 60 - 120 rpm | 60 - 120 rpm | to be chosen in such a way that plasticizing time is just within cooling time |