供应透明阻燃PC沙伯基础LEXAN940A
佛山市南海区兴诚盛塑胶经营部
中国 佛山
产品属性
图文详情
品牌推荐
品牌/厂家
基础创新塑料南沙
牌号
940A
用途级别
阻燃
产地
南海
熔体流动速率
11g/10min
密度
1.2g/cm3
拉伸强度
2350kg/cm2
弯曲强度
90kg/cm2
弯曲模量
2300kg/cm2
缺口冲击强度
65kg.cm/cm
LEXAN™ 940A resin 物性表
| 黄卡编号 | |
| 添加剂 |
|
| 特性 |
|
| 外观 |
|
| 加工方法 |
|
| 比重 | ASTM D792 | ||
| -- | 1.21 | g/cm³ | ASTM D792 |
| -- | 1.22 | g/cm³ | ASTM D792 |
| 特定体积 | 0.835 | cm³/g | ASTM D792 |
| Radiant Panel Listing (UL) | YES |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 | ASTM D570 | ||
| 24 hr | 0.15 | % | ASTM D570 |
| 平衡, 23°C | 0.35 | % | ASTM D570 |
| 平衡, 100°C | 0.58 | % | ASTM D570 |
| 洛氏硬度 | ASTM D785 | ||
| M 级 | 70 | ASTM D785 | |
| R 级 | 118 | ASTM D785 |
| 抗张强度 1 | ASTM D638 | ||
| 屈服 | 62.1 | MPa | ASTM D638 |
| 断裂 | 55.8 | MPa | ASTM D638 |
| 伸长率 2 | ASTM D638 | ||
| 屈服 | 7.0 | % | ASTM D638 |
| 断裂 | 90 | % | ASTM D638 |
| 弯曲模量 3(50.0 mm 跨距) | 2240 | MPa | ASTM D790 |
| 弯曲强度 4(屈服, 50.0 mm 跨距) | 91.0 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | ASTM D1044 |
| 悬壁梁缺口冲击强度 (23°C) | 640 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 3200 | J/m | ASTM D4812 |
| 落锤冲击 (23°C) | 169 | J | ASTM D3029 |
| 拉伸冲击强度 5 | 525 | kJ/m² | ASTM D1822 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 132 | °C | ASTM D648 |
| 维卡软化温度 | 152 | °C | ASTM D1525 6 |
| 线形热膨胀系数 - 流动 (-40 到 95°C) | 6.8E-5 | cm/cm/°C | ASTM E831 |
| 导热系数 | 0.19 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 体积电阻率 | > 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 (3.20 mm, in Air) | 17 | kV/mm | ASTM D149 |
| 介电常数 | ASTM D150 | ||
| 50 Hz | 3.01 | ASTM D150 | |
| 60 Hz | 3.01 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| 耗散因数 | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 0.010 | ASTM D150 | |
| 耐电弧性 7 | PLC 7 | ASTM D495 | |
| 相比耐漏电起痕指数(CTI) | PLC 2 | UL 746 | |
| 高电弧燃烧指数(HAI) | PLC 3 | UL 746 | |
| 高电压电弧起痕速率 (HVTR) | PLC 3 | UL 746 | |
| 热丝引燃 (HWI) | PLC 2 | UL 746 |
| UL 阻燃等级 | UL 94 | ||
| 1.47 mm | V-2 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| 极限氧指数 | 35 | % | ASTM D2863 |
| 折射率 | 1.586 | ASTM D542 | |
| 透射率 (2540 µm) | 85.0 | % | ASTM D1003 |
| 雾度 (2540 µm) | 1.0 | % | ASTM D1003 |
| 比重 | ASTM D792 | ||
| -- | 1.21 | g/cm³ | ASTM D792 |
| -- | 1.22 | g/cm³ | ASTM D792 |
| 特定体积 | 0.835 | cm³/g | ASTM D792 |
| Radiant Panel Listing (UL) | YES |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 | ASTM D570 | ||
| 24 hr | 0.15 | % | ASTM D570 |
| 平衡, 23°C | 0.35 | % | ASTM D570 |
| 平衡, 100°C | 0.58 | % | ASTM D570 |
| 洛氏硬度 | ASTM D785 | ||
| M 级 | 70 | ASTM D785 | |
| R 级 | 118 | ASTM D785 |
| 抗张强度 1 | ASTM D638 | ||
| 屈服 | 62.1 | MPa | ASTM D638 |
| 断裂 | 55.8 | MPa | ASTM D638 |
| 伸长率 2 | ASTM D638 | ||
| 屈服 | 7.0 | % | ASTM D638 |
| 断裂 | 90 | % | ASTM D638 |
| 弯曲模量 3(50.0 mm 跨距) | 2240 | MPa | ASTM D790 |
| 弯曲强度 4(屈服, 50.0 mm 跨距) | 91.0 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | ASTM D1044 |
| 悬壁梁缺口冲击强度 (23°C) | 640 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 3200 | J/m | ASTM D4812 |
| 落锤冲击 (23°C) | 169 | J | ASTM D3029 |
| 拉伸冲击强度 5 | 525 | kJ/m² | ASTM D1822 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 132 | °C | ASTM D648 |
| 维卡软化温度 | 152 | °C | ASTM D1525 6 |
| 线形热膨胀系数 - 流动 (-40 到 95°C) | 6.8E-5 | cm/cm/°C | ASTM E831 |
| 导热系数 | 0.19 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 体积电阻率 | > 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 (3.20 mm, in Air) | 17 | kV/mm | ASTM D149 |
| 介电常数 | ASTM D150 | ||
| 50 Hz | 3.01 | ASTM D150 | |
| 60 Hz | 3.01 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| 耗散因数 | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 0.010 | ASTM D150 | |
| 耐电弧性 7 | PLC 7 | ASTM D495 | |
| 相比耐漏电起痕指数(CTI) | PLC 2 | UL 746 | |
| 高电弧燃烧指数(HAI) | PLC 3 | UL 746 | |
| 高电压电弧起痕速率 (HVTR) | PLC 3 | UL 746 | |
| 热丝引燃 (HWI) | PLC 2 | UL 746 |
| UL 阻燃等级 | UL 94 | ||
| 1.47 mm | V-2 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| 极限氧指数 | 35 | % | ASTM D2863 |
| 折射率 | 1.586 | ASTM D542 | |
| 透射率 (2540 µm) | 85.0 | % | ASTM D1003 |
| 雾度 (2540 µm) | 1.0 | % | ASTM D1003 |
| 0.025 到 0.076 | mm |
供应PC 奇美食品级PC-110；耐候级PC-110U；
供应PC,940-701 GE防火V0黑色；
供应PC,940A-116 GE防火V0透明；
供应PC,943A,925U，945U沙特创新(原GE)V0防火抗紫外线；
供应PC,920A,940A,945A沙特创新(原GE)V0防火透明；
供应PC,920,940,945沙特创新(原GE)V0防火不透明；
供应PC,LS1,LS2,LS3沙特创新(原GE)光学级,鼠标，汽车灯罩专用；
供应PC,241R,243R,244R低粘度V0防火；高流动HF1110；超高粘度131R-111；
供应PC,920A-GY2A426T沙特创新(原GE)V0防火灰色；
供应PC,500R沙特创新(原GE)V0阻燃玻纤增强（10%GF）；
供应PC,EXL1414沙伯基础(原GE)耐寒（-40°至40°；透明，不透，黑色）；
供应PC,FXA1414沙伯基础(原GE)耐寒（-40°至95°；透明，不透，黑色）；
供应PC,940-GY2807沙特创新(原GE)V0防火灰色；
供应PC,141R,141，241沙特创新(原GE)中粘标准等级；
供应PC， 6465德国拜耳V0阻燃半透明；
供应PC，3108（耐冲FDA认证高粘挤出注塑级，透明，半透，不透）；
供应PC，2858,2458，2808德国拜耳（FDA认证中粘注塑级，透明，半透，不透）；
供应PC，2807,2607,2407德国拜耳（抗紫外线热稳定，透明，半透，不透）；
供应PC,2865德国拜耳透明阻燃；热稳定2805；耐冲2605；
供应PC，9415，9125德国拜耳玻纤增强V0阻燃（10%，20%不透明）；
供应PC泰国三菱耐候性S3000UR，S3000VR,S2000UR，S2000VR；
供应PC,GS2010MR2泰国三菱10%玻纤V2阻燃；
供应PC泰国三菱玻纤增强级7025G10，7025G15；光学级3215；
供应PC帝人L-1225Y,L-1250Y(V2高透明FDA)；LS-2250(V2耐磨)；LN-1250G(V0阻燃)；
供应PC韩国LG-DOW: 201-08，201-10，201-15，201-22；
供应PC,L-1250Y,L-1225Y新加坡帝人（注坯吹塑成型）；