耐高温 高韧性PPA/法国阿莫科/A-1133HS
东莞市禹泓塑料有限公司
中国 东莞
产品属性
图文详情
品牌推荐
品牌/厂家
法国阿莫科
牌号
A-1133HS
类型
正牌料
用途级别
注射级
产地
法国阿莫科
熔体流动速率
49g/10min
密度
1.48g/cm3
拉伸强度
13100kg/cm2
弯曲强度
148kg/cm2
缺口冲击强度
8.8kg.cm/cm
断裂伸长率
2.1%
成型收缩率
0.5%
热变形温度
285℃
阻燃等级
HB
PPA
耐高温
1PPA
高韧性
2PPA
良好的尺寸稳定性
3PPA
汽车内部零件
4PPA
工业零部件
Amodel® A-1133 HS
Polyphthalamide
33% Glass Fiber
Solvay Specialty Polymers
Product Description:
Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. Testing conducted on samples dry as molded and samples conditioned to 50% relative humidity in accordance with ISO-1110, Accelerated Method.
- Black: A-1133 HS BK 324
- Natural: A-1133 HS NT
Units: SI | English
| General | ||||
| Material Status |
| |||
| Literature 1 |
| |||
| UL Yellow Card 2 |
| |||
| Search for UL Yellow Card |
| |||
| Availability |
| |||
| Filler / Reinforcement |
| |||
| Additive |
| |||
| Features |
| |||
| Uses |
| |||
| RoHS Compliance |
| |||
| UL File NumberGlobal |
| |||
| Appearance |
| |||
| Forms |
| |||
| Processing Method |
| |||
| Multi-Point Data |
| |||
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
| Density | 1.48 | -- | g/cm3 | ISO 1183/A |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 4.0E-3 | -- | in/in | |
| Across Flow | 8.0E-3 | -- | in/in | |
| Water Absorption (24 hr) | 0.23 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
| Rockwell Hardness (R-Scale) | 125 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
| Tensile Modulus | ||||
| -- | 1.90E+6 | 1.90E+6 | psi | ASTM D638 |
| 73°F | 1.94E+6 | -- | psi | ISO 527-2 |
| 212°F | 1.57E+6 | -- | psi | ISO 527-2 |
| 302°F | 972000 | -- | psi | ISO 527-2 |
| 347°F | 624000 | -- | psi | ISO 527-2 |
| Tensile Stress | ||||
| Break, 73°F | 33800 | -- | psi | ISO 527-2 |
| Break, 212°F | 21500 | -- | psi | ISO 527-2 |
| Break, 302°F | 11600 | -- | psi | ISO 527-2 |
| Break, 347°F | 10400 | -- | psi | ISO 527-2 |
| -- | 32000 | 28000 | psi | ASTM D638 |
| Tensile Elongation | ||||
| Break | 2.5 | 2.1 | % | ASTM D638 |
| Break, 73°F | 2.5 | -- | % | ISO 527-2 |
| Break, 212°F | 2.9 | -- | % | ISO 527-2 |
| Break, 302°F | 8.7 | -- | % | ISO 527-2 |
| Break, 347°F | 8.5 | -- | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 1.65E+6 | 1.65E+6 | psi | ASTM D790 |
| 73°F | 1.68E+6 | -- | psi | ISO 178 |
| 212°F | 1.42E+6 | -- | psi | ISO 178 |
| 302°F | 580000 | -- | psi | ISO 178 |
| 347°F | 522000 | -- | psi | ISO 178 |
| Flexural Strength | ||||
| -- | 46000 | 36900 | psi | ASTM D790 |
| 73°F | 46300 | -- | psi | ISO 178 |
| 212°F | 32900 | -- | psi | ISO 178 |
| 302°F | 13500 | -- | psi | ISO 178 |
| 347°F | 11600 | -- | psi | ISO 178 |
| Compressive Strength | 26900 | -- | psi | ASTM D695 |
| Shear Strength | 14700 | 12900 | psi | ASTM D732 |
| Poisson's Ratio | 0.41 | -- | ASTM E132 | |
| Impact | Dry | Conditioned | Unit | Test Method |
| Charpy Notched Impact Strength (73°F) | 4.5 | -- | ft·lb/in2 | ISO 179/1eA |
| Charpy Unnotched Impact Strength (73°F) | 35 | -- | ft·lb/in2 | ISO 179/1eU |
| Notched Izod Impact | ||||
| -- | 1.5 | 1.1 | ft·lb/in | ASTM D256 |
| 73°F | 4.2 | -- | ft·lb/in2 | ISO 180/1A |
| Unnotched Izod Impact | ||||
| -- | 14 | -- | ft·lb/in | ASTM D256 |
| 73°F | 23 | -- | ft·lb/in2 | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
| Deflection Temperature Under Load | ||||
| 66 psi, Annealed, 0.126 in | 567 | -- | °F | ASTM D648 |
| 264 psi, Unannealed | 536 | -- | °F | ISO 75-2/A |
| 264 psi, Annealed, 0.126 in | 545 | -- | °F | ASTM D648 |
| Continuous Use Temperature | ASTM D3045 | |||
| -- 3 | 327 | -- | °F | |
| -- 4 | 365 | -- | °F | |
| Melting Temperature | 595 | -- | °F | ASTM D570, ISO 11357-3 |
| CLTE | ASTM E831 | |||
| Flow : 32 to 212°F | 1.3E-5 | -- | in/in/°F | |
| Flow : 212 to 392°F | 1.5E-5 | -- | in/in/°F | |
| Transverse : 32 to 212°F | 3.1E-5 | -- | in/in/°F | |
| Transverse : 212 to 392°F | 6.4E-5 | -- | in/in/°F |
| Electrical | Dry | Conditioned | Unit | Test Method |
| Volume Resistivity | 1.0E+16 | 2.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (0.126 in) | 530 | 530 | V/mil | ASTM D149 |
| Dielectric Constant | ASTM D150 | |||
| 60 Hz | 4.40 | 4.70 | ||
| 1 MHz | 4.20 | 4.30 | ||
| Dissipation Factor | ASTM D150 | |||
| 60 Hz | 5.0E-3 | 9.0E-3 | ||
| 1 MHz | 0.017 | 0.022 | ||
| Arc Resistance | 140 | 120 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 550 | 550 | V | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
| Flame Rating 5 (0.126 in) | HB | -- | UL 94 |
| Optical | Dry | Conditioned | Unit | Test Method |
| Transmittance 6 | ASTM D1003 | |||
| 1070 nm : 63.0 mil | > 30 | -- | % | |
| 940 nm : 63.0 mil | > 30 | -- | % |
| Additional Information | ||||
| Conditioned | Conditioned to 50% RH in accordance with ISO-1110, Accelerated Method | |||
| Injection | Dry | Unit | |
| Drying Temperature | 248 | °F | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.045 | % | |
| Rear Temperature | 580 to 605 | °F | |
| Front Temperature | 600 to 625 | °F | |
| Processing (Melt) Temp | 610 to 650 | °F | |
| Mold Temperature | 275 | °F | |
| Injection Notes | |||