Physical Properties物理性质

Metric公制数据

English英制数据

Comments测试方法

Density密度

1.49 g/cc

0.0538 lb/in³

DAM; ISO 1183

Filler Content填料含量

43 %

43 %

DAM

Water Absorption吸水率

2.2 %
@Thickness 1.00 mm,
Temperature 23.0 °C

2.2 %
@Thickness 0.0394 in,
Temperature 73.4 °F

Equilibrium 50%RH; DAM; ISO 62, Similar to

7.6 %
@Thickness 1.00 mm,
Temperature 23.0 °C

7.6 %
@Thickness 0.0394 in,
Temperature 73.4 °F

Saturation, immersed; DAM; ISO 62, Similar to

Linear Mold Shrinkage, Flow线性收缩率/流动

0.0030 cm/cm
@Thickness 2.00 mm

0.0030 in/in
@Thickness 0.0787 in

Parallel; DAM; ISO 294-4

Linear Mold Shrinkage, Transverse线性收缩率/横向

0.0090 cm/cm
@Thickness 2.00 mm

0.0090 in/in
@Thickness 0.0787 in

Normal; DAM; ISO 294-4

Mechanical Properties力学性能

Metric公制数据

English英制数据

Comments测试方法

Tensile Strength at Break断裂拉伸强度

160 MPa
@Temperature 23.0 °C

23200 psi
@Temperature 73.4 °F

50%RH; ISO 527

225 MPa
@Temperature 23.0 °C

32600 psi
@Temperature 73.4 °F

DAM; ISO 527

Elongation at Break断裂伸长率

2.5 %
@Temperature 23.0 °C

2.5 %
@Temperature 73.4 °F

DAM; ISO 527

3.5 %
@Temperature 23.0 °C

3.5 %
@Temperature 73.4 °F

50%RH; ISO 527

Tensile Modulus拉伸模量

11.0 GPa
@Temperature 23.0 °C

1600 ksi
@Temperature 73.4 °F

50%RH; ISO 527

14.0 GPa
@Temperature 23.0 °C

2030 ksi
@Temperature 73.4 °F

DAM; ISO 527

Izod Impact, Notched悬臂梁缺口冲击强度 (ISO)

14.0 kJ/m²
@Temperature 23.0 °C

6.66 ft-lb/in²
@Temperature 73.4 °F

DAM; ISO 180/1A

16.0 kJ/m²
@Temperature 23.0 °C

7.61 ft-lb/in²
@Temperature 73.4 °F

50%RH; ISO 180/1A

Charpy Impact Unnotched夏比缺口试样冲击

9.00 J/cm²
@Temperature 23.0 °C

42.8 ft-lb/in²
@Temperature 73.4 °F

DAM; ISO 179/1eU

9.50 J/cm²
@Temperature 23.0 °C

45.2 ft-lb/in²
@Temperature 73.4 °F

50%RH; ISO 179/1eU