NORYL GTX™ GTX8120P
PPE/PA
沙特基础 (SABIC)
产品描述
NORYL GTX™ 812OP resin is a 20% glass reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This extrudable grade has excellent chemical resistance and high heat resistance. . NORYL GTX8120P resin is anodizable, has low thermal conductivity and is an excellent candidate for extruded thermal break applications.
基本信息
| 原厂资料 | ||||
| 产品特性 | 高强度高刚性耐热尺寸稳定低翘曲低收缩耐化学性耐水解低密度低吸湿性填充增强 | |||
| 成型方式 | 挤出 | |||
| 增强填充 | 20% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.24 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
280°C/10.0 kg | 12 cm³/10 min | ISO 1133 | |
吸水率 | 2.5 % | ISO 62 | 23°C/sat |
吸湿率 | 1 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸模量 | 6800 Mpa | ISO 527 | 1 mm/min |
拉伸强度 | |||
屈服(yld) | 125 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 125 Mpa | ISO 527 | 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 3 % | ISO 527 | 5 mm/min |
断裂(brk) | 3.5 % | ISO 527 | 5 mm/min |
弯曲模量 | 5000 Mpa | ISO 178 | 2 mm/min |
NORYL CN1134沙特基础 (SABIC)PPE/PS
NORYL HM3020H沙特基础 (SABIC)PPE/PS
NORYL HM4025H沙特基础 (SABIC)PPE/PS
NORYL NCF1010沙特基础 (SABIC)PPE/PS
NORYL NF2020沙特基础 (SABIC)PPE/PS
NORYL NFV1030沙特基础 (SABIC)PPE/PS
NORYL PCN2910沙特基础 (SABIC)PPE/PS
NORYL PX0844沙特基础 (SABIC)PPE/PS
NORYL PX0888沙特基础 (SABIC)PPE/PS
NORYL PX2956沙特基础 (SABIC)PPE/PS
NORYL RN0206沙特基础 (SABIC)PPE/PS
NORYL RN0401沙特基础 (SABIC)PPE/PS
NORYL SE100X沙特基础 (SABIC)PPE/PS
NORYL TPN9221沙特基础 (SABIC)PPE/PS
NORYL ZM3242沙特基础 (SABIC)PPE/PS
NORYL ZM3640沙特基础 (SABIC)PPE/PS
NORYL EM7430沙特基础 (SABIC)PPE/PS
NORYL EXNL0143沙特基础 (SABIC)PPE/PS
NORYL EXNL0357沙特基础 (SABIC)PPE/PS
NORYL EZ250沙特基础 (SABIC)PPE/PS
NORYL FP6130沙特基础 (SABIC)PPE/PS
NORYL HS2000X沙特基础 (SABIC)PPE/PS
NORYL NH7010HF沙特基础 (SABIC)PPE/PS
NORYL PN275沙特基础 (SABIC)PPE/PS
NORYL PN275F沙特基础 (SABIC)PPE/PS
NORYL PX1543F沙特基础 (SABIC)PPE/PS
NORYL PX4605沙特基础 (SABIC)PPE/PS
NORYL SE100HX沙特基础 (SABIC)PPE/PS
NORYL GTX GTX6203沙特基础 (SABIC)PPE/PA
NORYL GTX GTX902D沙特基础 (SABIC)PPE/PA
NORYL GTX GTX918WR沙特基础 (SABIC)PPE/PA
NORYL GTX GTX934沙特基础 (SABIC)PPE/PA
NORYL GTX GTX975沙特基础 (SABIC)PPE/PA
NORYL GTX GTX989沙特基础 (SABIC)PPE/PA
NORYL GTX GTX673沙特基础 (SABIC)PPE/PA
NORYL GTX NX0031沙特基础 (SABIC)PPE/PA
NORYL GTX GTX8120P沙特基础 (SABIC)PPE/PA
NORYL GTX GTX830 - Europe沙特基础 (SABIC)PPE/PA
NORYL GTX GTX830 - Asia沙特基础 (SABIC)PPE/PA
NORYL GTX GTX918W - Europe沙特基础 (SABIC)PPE/PA
NORYL GTX GTX964沙特基础 (SABIC)PPE/PA
NORYL GTX GTX679沙特基础 (SABIC)PPE/PA
NORYL GTX GTX951W沙特基础 (SABIC)PPE/PA
NORYL GTX GTX987沙特基础 (SABIC)PPE/PA
NORYL GTX GTX902沙特基础 (SABIC)PPE/PA
NORYL GTX GTX910沙特基础 (SABIC)PPE/PA
NORYL GTX GTX626沙特基础 (SABIC)PPE/PA
NORYL GTX RNX130沙特基础 (SABIC)PPE/PA
NORYL PPX PPX630沙特基础 (SABIC)PPE/PP
NORYL PPX PPX7110沙特基础 (SABIC)PPE/PP
NORYL PPX PPX830沙特基础 (SABIC)PPE/PP
NORYL PPX PPX630F沙特基础 (SABIC)PPE/PP
NORYL PPX PPX640F沙特基础 (SABIC)PPE/PP
NORYL PPX PPX7115F沙特基础 (SABIC)PPE/PP
NORYL GTX GTX918W - Asia沙特基础 (SABIC)PPE/PA
1.（PPO或PPE)又称聚亚苯基氧PPO塑料（聚苯醚），亦称聚苯醚b或聚亚苯基氧，是世界五大通用工程塑料。其化学名称为聚2,6-二甲基-1,4-苯醚，由2,6-二甲基苯酚氧化缩聚制成，常态呈土黄色粉末或白色颗粒状，主要应用于电子电器、汽车、机械制造领域。该材料以刚性大、耐热性高著称，长期使用温度范围-127℃至121℃，负荷变形温度可达190℃以上。具有低吸水性（0.06%）、电绝缘性（介电性能居工程塑料首位）及耐腐蚀特性。改性品种MPPO通过共混HIPS等材料提升加工性能并保持耐热性（玻璃化温度211℃）与阻燃性。制品应用于连接器、仪表板、齿轮等部件，成型需控制280-330℃温度并预干燥处理.
2.PPE/PPO，别名聚苯撑醚、聚苯醚，是一种热塑性工程塑料。该材料主要应用于家庭用品（洗碗机、洗衣机）、电器设备（控制器壳体、光纤连接器）及耐高压电器部件（如彩电行输出变压器）的制造，并在新能源电池、光伏、IC盘等领域有延伸应用。商业产品通常混入PS、PA等其他热塑性材料以改善加工性能，混合比例影响其特性。PPE塑胶具有电绝缘性，其介电常数和介电损耗角正切为工程塑料中小，体积电阻率高，且在温度、湿度变化下保持稳定。制品几何稳定性，吸湿率低，玻璃化温度达211℃，热水浸泡后物理性能下降幅度小。注塑加工需100℃预干燥2-4小时，熔融温度240-320℃，注塑压力600-1500 Bar，适配柄型及扇形浇口，添加玻璃纤维可使收缩率降至0.2%
3.（PPO或PPE)注塑模工艺条件
乾燥处理：建议在成型加工前进行2-4小时、100度的乾燥处理。
熔融温度：240-320度
模具温度：60-105度
注塑压力：600-1500 Bar
浇道和浇口：可以使用所有类型的浇口，特别适合于使用柄型浇口和扇形浇口。
4.（PPO或PPE)中国一级代理商包括东莞市东利塑胶原料有限公司-毛总15322412218/15807693310，供应全系列原厂原包