Lupolen UHM 5000
PE, UHMWPE
利安德巴塞尔(LyondellBasell)
产品描述
Lupolen UHM 5000 is an ultra high molecular weight polyethylene (UHMW PE) with an average molecular weight of 5 million. The long molecular chains leed to unique properties:
Highest abrasion resistance of any thermoplastic materials, excellent impact strength, low friction, good chemical resistance and stress crack resistance.
Lupolen UHM 5000 is used in compression molding and ram extrusion processes. The material is supplied in form of coarse natural powder. The larger particle size and the very low fines content result in good free flowing property and less dust generation during handling and processing.
This grade is not intended for medical and pharmaceutical applications.
基本信息
| 原厂资料 | ||||
| 产品特性 | 高冲击耐磨低摩擦ESCR耐化学性 | |||
| 颜色形状 | 粉末状本色 | |||
| 成型方式 | 挤出模压 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.931 g/cm³ | ISO 1183 | |
粘度 | 2200 cm³/g | ISO 1628 | Intrinsic Viscosity |
粘度 | 2500 cm³/g | ISO 1628 | Viscosity Number |
粒子大小 | 500 micrometer | Internal | |
堆积(视)密度 | 0.45 g/cm³ | ISO 60 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸模量 | 800 Mpa | ISO 527-1/-2 | 23 °C |
拉伸强度 | |||
屈服(yld) | 20 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 12 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
拉伸蠕变模量 | |||
1h | 550 Mpa | ISO 899-1 | 2 MPa |
1000h | 300 Mpa | ISO 899-1 | 2 MPa |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 190 kJ/m² | ISO 179 | Double Notch according ISO 11542-2 Annex B |
23℃ (73℉) | NB kJ/m² | ISO 179-1/1eA | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 63 D | ISO 868 | 15 sec |
邵氏硬度 D | 65 D | ISO 868 | 3 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 45 °C | ISO 75-1/-2 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 68 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 82 °C | ISO 306/B50 | |
熔融温度(Tm) | 135 °C | DSC |
GUR 2122塞拉尼斯(Celanese)PE, UHMWPE
GUR 2122-5塞拉尼斯(Celanese)PE, UHMWPE
GUR 2126塞拉尼斯(Celanese)PE, UHMWPE
GUR 4012塞拉尼斯(Celanese)PE, UHMWPE
GUR 4012 F塞拉尼斯(Celanese)PE, UHMWPE
GUR 4020-3塞拉尼斯(Celanese)PE, UHMWPE
GUR 4022塞拉尼斯(Celanese)PE, UHMWPE
GUR 4022-6塞拉尼斯(Celanese)PE, UHMWPE
GUR 4032塞拉尼斯(Celanese)PE, UHMWPE
GUR 4050-3塞拉尼斯(Celanese)PE, UHMWPE
GUR 4056-3塞拉尼斯(Celanese)PE, UHMWPE
GUR 4112塞拉尼斯(Celanese)PE, UHMWPE
GUR 4113塞拉尼斯(Celanese)PE, UHMWPE
GUR 4120塞拉尼斯(Celanese)PE, UHMWPE
GUR 4122塞拉尼斯(Celanese)PE, UHMWPE
GUR 4122-5塞拉尼斯(Celanese)PE, UHMWPE
GUR 4130塞拉尼斯(Celanese)PE, UHMWPE
GUR 4150塞拉尼斯(Celanese)PE, UHMWPE
GUR 4150-3塞拉尼斯(Celanese)PE, UHMWPE
GUR 4152塞拉尼斯(Celanese)PE, UHMWPE
GUR 4170塞拉尼斯(Celanese)PE, UHMWPE
GUR 4523塞拉尼斯(Celanese)PE, UHMWPE
GUR 4550塞拉尼斯(Celanese)PE, UHMWPE
GUR 5113塞拉尼斯(Celanese)PE, UHMWPE
GUR 5129塞拉尼斯(Celanese)PE, UHMWPE
GUR 5523塞拉尼斯(Celanese)PE, UHMWPE
GUR X 161塞拉尼斯(Celanese)PE, UHMWPE
GUR X 195塞拉尼斯(Celanese)PE, UHMWPE
GUR X 201塞拉尼斯(Celanese)PE, UHMWPE
GUR X 204塞拉尼斯(Celanese)PE, UHMWPE
GUR X 205 塞拉尼斯(Celanese) PE, UHMWPE
GUR X 214 塞拉尼斯(Celanese) PE, UHMWPE
GUR X 217 塞拉尼斯(Celanese) PE, UHMWPE
由于超高分子量聚乙烯（UHMW-PE）熔融状态的粘度高达108Pa*s，流动性极差，其熔体指数几乎为零，所以很难用一般的机械加工方法进行加工。超高分子量聚乙烯（UHMW-PE）的加工技术得到了迅速发展，通过对普通加工设备的改造，已使超高分子量聚乙烯（UHMW-PE）由最初的压制-烧结成型发展为挤出、吹塑和注射成型以及其它特殊方法的成型。
一般
1.压制烧结
(1)压制烧结是超高分子量聚乙烯（UHMW-PE）最原始的加工方法。此法生产效率颇低，易发生氧化和降解。为了提高生产效率，可采用直接电加热法
(2)超高速熔结加工法，采用叶片式混合机，叶片旋转的最大速度可达150m/s，使物料仅在几秒内就可升至加工温度。
2.挤出成型
挤出成型设备主要有柱塞挤出机、单螺杆挤出机和双螺杆挤出机。双螺杆挤出多采用同向旋转双螺杆挤出机。
(3)注塑成型
日本三井石油化工公司于1974年开发了注塑成型工艺，并于1976年实现了商业化，之后又开发了往复式螺杆注塑成型技术。1985年美国Hoechst公司也实现了超高分子量聚乙烯（UHMW-PE）的螺杆注塑成型工艺。我国1983年对国产XS-ZY-125A型注射机进行了改造，成功地注射出啤酒罐装生产线用超高分子量聚乙烯（UHMW-PE）托轮、水泵用轴套等。
(4)吹塑成型
超高分子量聚乙烯（UHMW-PE）加工时，当物料从口模挤出后，因弹性恢复而产生一定的回缩，并且几乎不发生下垂现象，故为中空容器，特别是大型容器，如油箱、大桶的吹塑创造了有利的条件。超高分子量聚乙烯（UHMW-PE）吹塑成型还可导致纵横方向强度均衡的高性能薄膜，从而解决了HDPE薄膜长期以来存在的纵横方向强度不一致，容易造成纵向破坏的问题