鞋底发泡 VA含量18% EVA UE629 台湾台聚
产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
其它性能 | 射出 | | ASTM D-638/D-882 | 220 | % |
铸膜成型 | | ASTM D-638/D-882 | 750 | % |
薄膜 | MD | | ASTM D-638/D-882 | 250 | kg/cm2 |
TD | | ASTM D-638/D-882 | 240 | kg/cm2 |
薄膜 | MD | | ASTM D-638/D-882 | 480 | % |
TD | | ASTM D-638/D-882 | 640 | % |
机械性能 | 冲击强度 | | ASTM D-1709 | 430 | G/F50 |
其它性能 | 射出 | | ASTM D-638/D-882 | 117 | kg/cm2 |
VA含量 | | ASTM USIFE | 18 | % |
密度 | | ASTM D-1505 | 0.939 | g/cm3 |
融化点 | | ASTM D-2117 | 86 | ℃ |
VICAT 软化点 | | ASTM D-1525 | 64 | ℃ |
熔融指数 | | ASTM D-1238 | 2.5 | g/10min |
低温易脆性 | | ASTM D-746 | <-76 | ℃/F50 |
硬度 | | ASTM D-2240 | 31 | Shore D |
铸膜成型 | | ASTM D-638/D-882 | 180 | kg/cm2 |