LCP耐磨级 LCP防火LCP 1000美国杜邦10105
②原料技术数据
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
黑色 |
ASTM D-792 |
1.62 |
--- |
| 泰伯摩擦 |
--- |
ASTM D-1044 |
63 |
mg |
| 模缩率 |
流向1.6mm |
ASTM D-955 |
-0.1 |
% |
| 模缩率 |
流向3.2mm |
ASTM D-955 |
0 |
% |
| 模缩率 |
横向1.6mm |
ASTM D-955 |
0.9 |
% |
| 机械性能 |
模缩率 |
横向3.2mm |
ASTM D-955 |
0.8 |
% |
| 洛氏硬度 |
Scale M |
ASTM D-785 |
63 |
--- |
| 冲击下机械性能 |
--- |
UL 746B |
210 |
ºC |
| 拉伸强度 |
23℃,1.6mm |
ASTM D-638 |
173 |
MPa |
| 拉伸强度 |
23℃,3.2mm |
ASTM D-638 |
150 |
MPa |
| 断裂伸长率 |
23℃,1.6mm |
ASTM D-638 |
1.6 |
% |
| 断裂伸长率 |
23℃,3.2mm |
ASTM D-638 |
1.7 |
% |
| 拉伸模量 |
23℃,1.6mm |
ASTM D-638 |
19306 |
MPa |
| 拉伸模量 |
23℃,3.2mm |
ASTM D-638 |
18000 |
MPa |
| 弯曲模量 |
23℃,0.8mm |
ASTM D-790 |
18000 |
MPa |
| 弯曲模量 |
23℃,1.6mm |
ASTM D-790 |
14000 |
MPa |