产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
基本性能 | 熔体流动速率 | 300℃/1.2kg | ASTM D-1238 | 30 | g/10min |
平衡吸水率 | 23℃,相对湿度50% | ASTM D-570 | 0.32 | % |
吸水率 | 24hr,23℃ | ASTM D-570 | 0.15 | % |
物理性能 | 雾度 | | ASTM D-1003 | 0.7-1.5 | % |
透光率 | | ASTM D-1003 | 89 | % |
比重 | | ASTM D-792 | 1200 | kg/m3 |
模具收缩率 | | ASTM D-955 | 0.005-0.007 | in/in |
阻燃等级 | 3.2mm | UL 94 | HB | |
阻燃等级 | 1.6mm | UL 94 | HB | |
机械性能 | 弯曲强度 | | ASTM D-790 | 96 | MPa |
弯曲模量 | | ASTM D-790 | 2410 | MPa |
拉伸强度 | 屈服点 | 50mm/min | ASTM D-638 | 60 | MPa |
断裂点 | - | ASTM D-638 | 61 | MPa |
伸长率 | 屈服点 | | ASTM D-638 | 6 | % |
断裂点 | | ASTM D-638 | 150 | % |
冲击强度 | 23℃ | ASTM D-256 | 未破裂 | |
拉伸模量 | | ASTM D-638 | 2340 | MPa |
折射率 | | ASTM D-542 | 1.586 | |
缺口冲击强度 | 23℃ | ASTM D-256 | 700 | j/m |
电气性能 | 体积电阻 | 23℃,干 | ASTM D-257 | 2.0×1017 | Ω.cm |
辉光灯丝测试 | 2mm,5s | IEC 695-2-1 | 850 | ℃ |
对比电弧径迹指数 | 2mm | IEC 112 | 250 | V |
介电强度 | 60Hz | ASTM D-149 | 17 | V/mil |
球状压痕温度 | | IEC 598-1 | >125 | ℃ |
损耗因素 | 60Hz | ASTM D-150 | 0.001 | |
热性能 | 热变形温度 | 退火@0.45MPa | ASTM D-648 | 139 | ℃ |
热变形温度 | 退火@1.82MPa | ASTM D-648 | 136 | ℃ |
线性热收缩率 | -40℃~82℃ | ASTM D-696 | 68×10-6 | mm/mm/℃ |
平均燃烧系数 | | ASTM D-635 | mm | 25 |
热变形温度 | 未退火@1.82MPa | ASTM D-648 | 122 | ℃ |
维卡软化点 | 50℃/小时,50n重 | ASTM D-1525 | 144 | ℃ |
其它性能 | 需氧系数 | | ASTM D-2863 | 26 | % |