PRODUCT DESCRIPTION产品描述J-800A/B is a two part epoxy paste adhesive. It is an excellent structural adhesive to bond metals, composite laminates, most thermoplastics, and many other dissimilar materials. J-800A/B是一种双组分环氧树脂膏状胶粘剂。它是一种粘结金属材料，复合材料薄片，绝大多数的热塑性塑料和一些其他不同材料的优异的结构胶。 Major Features主要优点l
Long open time操作时间长l
High shear and peel strength高的剪切与高剥离强度l
Excellent low temperature properties优异的低温性能l
Room temperature cure常温固化l
Controlled flow流动性容易控制 PROPERTIES OF UNCURED MATERIAL固化前材料性能Property性能Test Method测试方法J-800AJ-800BColor/appearance颜色Visual目视Creamy white, viscous/liquid膏状白色粘稠液体Amber Liquid琥珀色液体SpecificGrav密度, g/ccASTM D-7921.121.10Viscosity粘度(cP), 25ºCASTM D-239360,000 - 100,0008,000 - 12,000 TYPICAL CURED PROPERTIES固化后属性Property性能Test Method测试方法Test Value测试值Hardness, casting after 15 minutes,  Shore D邵氏硬度，浇铸15分钟后D-224075Ultimate Tensile Strength极限抗张强度, psiD-6385200Elongation生长率, %D-6387Modulus模量(psi)D-638400, 000T- Peel Test  剥离测试(pli)D-187650-60Lap shear strength搭接剪切强度, psi at 25CASTM D-1002 Galvanized Steel镀锌钢 2500Fibre reinforced composite纤维增强复合材料 1500Mineral filled PET plastics矿物填充PET塑料 800Aluminum (primered)铝 5000Aluminum (acid etched)铝（酸腐蚀） 4200Effects of application temperature on lap shear strength(LSS ) by ASTM D-1002温度对搭接剪切的影响Load applied 10 minutes after specimens reach test temperature当样品达到测试温度后10分钟
Test TemperatureLSS Value, psiAl/Al -60ºC4700Al/Al 82  ºC1500Al/Al 121 ºC500Al/Al 30 days salt spray4000Al/Al 30 days @ 60ºC/100% RH3500Directions for use使用方法Reaction Ratio (by weight)反应重量比 100A/49BReaction Ratio (by volume)反应体积比 100A/50BPot Life (100 grams) 25°C使用时间（100克）ASTM D-247130 minutesPot Life (20 grams) 25°C使用时间（20克） 60 minutes Curing time table固化进度表:3-5 days at 77?F. or elevated temperatures for accelerated cure.在25摄氏度下3-5天。或者在升高的温度下加速固化 Shelf Life保质期
Provided this material is stored under the recommended storage condition in the original container, it will remain in useable condition for from date of shipping.若该产品按照上述要求存储，并且是保存在原装容器内，从发货之日起，在一年内可以使用。