| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率g/10 minASTM D-12385 |
| 物理性能吸收率23°C,60%RHASTM D-5700.25% |
| 成型收缩率t3mm,直径100mm1.7% |
| 填充材料含有率High% |
| 比重ASTM D-7921.36 |
| 机械性能拉伸冲击强度t3.2mm S typeASTM D-1822220kgf.cm/cm2 |
| 拉伸强度23℃ASTM D-638380kgf/cm2 |
| 弯曲强度23℃ASTM D-790490kgf/cm2 |
| IZOD冲击强度Notch t3.2mmASTM D-25612kgf.cm/cm |
| 伸缩率23℃ASTM D-638>=200% |
| 洛氏硬度M scaleASTM D-785M77 |
| 曲折弹性率23℃ASTM D-7901.40×104kgf/cm2 |
| 电气性能表面电阻率ASTM D-2571×1016Ω |
| 体积电阻率ASTM D-2571×1014Ω.cm |
| 热性能燃烧性t0.8mmUL 94HB |
| 热变形温度18.6kgf/cm2ASTM D-64888℃ |
| 热变形温度4.6kgf/cm2ASTM D-648143℃ |
| 熔点10C°/minDSC Method165℃ |
| 线膨胀系数20C°-80CASTM D-69613×10-5cm/cm/℃ |