性能项目试验条件[状态]测试方法测试数据数据单位 |
物理性能流动系数200°C/5kgASTM D-1238(G)2.2g/10min |
成型收缩率ASTM D-9550.4~0.7% |
比重ASTM D-7921.11 |
机械性能伸张率(破断点)50mm/minASTM D-63840% |
张力摸数1mm/minASTM D-63822200(2180)kg/cm2(MPa) |
洛氏强度R-ScaleASTM D-785112 |
弯曲强度15mm/minASTM D-790800(78)kg/cm2(MPa) |
IZOD冲击强度1/4",23°CASTM D-25610(100)kg.cm/cm(J/m) |
伸张率(抗拒点)50mm/minASTM D-638≥6% |
张力强度50mm/minASTM D-638520(51)kg/cm2(MPa) |
弯曲摸数15mm/minASTM D-79025000(2450)kg/cm2(MPa) |
热性能燃烧性1/8"IEC707-mm/min |
热变形温度4.6kg/cm21/4"annealed(unannealed)ASTM D-64895(90)℃ |
热变形形温度1.86kgf/cm21/4ASTM D-64889(89)℃ |
微卡软化点1kg/120℃/h(5kg/50℃/h)ASTM D-1525100(93)℃ |
燃烧性1/8"UL-94HBclass |