PA12 日本宇部 3024U
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 成型收缩率 | | UBEmethod | 1.6 | % |
| 成型收缩率 | | UBEmethod | 1.0 | % |
| 吸水率 | | ASTM D-570 | 1.5 | % |
| 吸水率 | | ASTM D-570 | 0.25 | % |
| 比重 | | ASTM D-792 | 1.02 |
| 弯曲强度 | 23° | ASTM D-790 | 400 | kgf/cm2 |
| 抗冲击强度 | -30° | ASTM D-256 | 5.0 | kgf.cm/cm |
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 130 | kgf/cm2 |
| 抗冲击强度 | 23° | ASTM D-256 | 50 | kgf.cm/cm |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 400 | kgf/cm2 |
| 弯曲弹性率 | -30° | ASTM D-790 | 17500 | kgf/cm2 |
| 断裂下的延伸率 | 23° | ASTM D-638 | ＞250 | % |
| 弯曲强度 | 80° | ASTM D-790 | 180 | kgf/cm2 |
| 屈服下的伸张强度 | -30° | ASTM D-638 | 800 | kgf/cm2 |
| 屈服下的延伸率 | 23° | ASTM D-638 | 10 | % |
| 弯曲弹性率 | 23° | ASTM D-790 | 10500 | kgf/cm2 |
| 弯曲强度 | -30° | ASTM D-790 | 900 | kgf/cm2 |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 460 | kgf/cm2 |
| 屈服下的延伸率 | 23° | ASTM D-638 | 14 | % |
| 断裂下的伸张强度 | 23° | ASTM D-638 | ＞570 | kgf/cm2 |
| 弯曲强度 | 23° | ASTM D-790 | 610 | kgf/cm2 |
| 屈服下的伸张强度 | 80° | ASTM D-638 | 200 | kgf/cm2 |
| 抗冲击强度 | 23° | ASTM D-256 | 6.0 | kgf.cm/cm |
| 挤剪强度 | 23° | ASTM D-732 | 350 | kgf/cm2 |
| 弯曲弹性率 | 23° | ASTM D-790 | 15500 | kgf/cm2 |
| 硬度(洛氏、布氏) | 23° | ASTM D-785 | 110 |
| 硬度(洛氏、布氏) | 23° | ASTM D-785 | 85 |
| 弯曲弹性率 | 80° | ASTM D-790 | 3500 | kgf/cm2 |
| TABER磨耗率 | | ASTM D-1044 | 5 | mg |
| 弯曲弹性率 | 80° | ASTM D-790 | 4000 | kgf/cm2 |
| 断裂下的伸张强度 | 23° | ASTM D-638 | ＞520 | kgf/cm2 |
| 介电常数 | 103HZ | ASTM D-150 | 3.5 |
| 抗电弧强度 | | ASTM D-495 | 180 | S |
| 体积电阻率 | | ASTM D-257 | 1015 | Ω.cm |
| 介电损耗 | 106HZ | ASTM D-150 | 0.02 |
| 体积电阻率 | | ASTM D-257 | 1014 | Ω.cm |
| 绝缘耐力 | | ASTM D-149 | 30 | KV/mm |
| 介电常数 | 60HZ | ASTM D-150 | 3.7 |
| IEC电路 | | UL746 | 600+ | V |
| 介电损耗 | 103HZ | ASTM D-150 | 0.03 |
| 介电常数 | 106HZ | ASTM D-150 | 3.1 |
| 介电损耗 | 60HZ | ASTM D-150 | 0.03 |
| 线性热膨胀系数 | | ASTM D-696 | 10 | X的10-5cm/cm/°C |
| 燃烧率 | | UL94 | HB |
| 熔点 | DSC | | 176-180 | °C |
| 热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 145 | °C |