我公司现货代理，PA66 408 409 ST801
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 吸水率 | 饱和(23℃) | ASTM D-570 | DAM｜50%RH,7.0｜- | % |
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | DAM｜50%RH,1.2｜- | % |
| 比重 | | ASTM D-792 | DAM｜50%RH,1.09｜1.09 |
| 断裂伸长率 | 23℃ | ASTM D-638 | DAM｜50%RH,80｜270 | % |
| 揉曲模量 | 23℃ | ASTM D-790 | DAM｜50%RH,1965｜1103 | MPa |
| 洛氏硬度M | | ASTM D-785 | DAM｜50%RH,M71｜M50 |
| 埃佐冲击强度 | 23℃ | ASTM D-256 | DAM｜50%RH,230｜240 | j/m |
| 硬度计硬度 | | ASTM D-676 | DAM｜50%RH,83｜76 |
| 洛氏硬度R | | ASTM D-785 | DAM｜50%RH,R115｜R102 |
| 屈服伸长率 | | ASTM D-638 | DAM｜50%RH,5｜15 | % |
| 屈服强度 | 23℃ | | DAM｜50%RH,60.7｜51.7 | MPa |
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | DAM｜50%RH,550｜1680 | KJ/m2 |
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | DAM｜50%RH,189｜265 | KJ/m2 |
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜50%RH,62.1｜51.7 | MPa |
| 体积电阻率 | | ASTM D-257 | DAM｜50%RH,10,13,｜10,13 | Ω.cm |
| 介电常数 | 103Hz(cps) | ASTM D-150 | DAM｜50%RH,3.1｜4.8 |
| 耗散因数 | 100Hz(cps) | ASTM D-150 | DAM｜50%RH,0.02｜0.1 |
| 耗散因数 | 103Hz(cps) | ASTM D-150 | DAM｜50%RH,0.02｜0.11 |
| 耗散因数 | 106Hz(cps) | ASTM D-150 | DAM｜50%RH,0.02｜0.10 |
| 介电常数 | 100Hz(cps) | ASTM D-150 | DAM｜50%RH,3.1｜5.9 |
| 介电常数 | 106Hz(cps) | ASTM D-150 | DAM｜50%RH,2.9｜3.3 |
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | DAM｜50%RH,230｜- | ℃ |
| UL可燃性导级 | | UL 94 | DAM｜50%RH,94｜HB |
| 熔点结晶 | | ASTM D-2177 | DAM｜50%RH,270｜- | ℃ |
| 线性热膨胀系数 | | ASTM D-696 | DAM｜50%RH,7×10,-5,｜- | m/m/℃ |
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | DAM｜50%RH,1.4｜- | % |
| 熔点 | Fisher Johns法 | ASTM D-789 | DAM｜50%RH,255｜255 | ℃ |
| 热畸变温度 | 18×106Pa | ASTM D-648 | DAM｜50%RH,75｜- | ℃ |
| 脆化温度 | | ASTM D-746 | DAM｜50%RH,-104｜-84 | ℃ |
| 需氧指数 | | ASTM D-2863 | DAM｜50%RH,19｜20 | % |