ABS 700
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.30 | % |
| 熔体流动速率 | 220℃/10.0kg | ISO 1133 | 40 | g/10min |
| 比重 | | ASTM D-792 | 1.05 | g/cm3 |
| | | ISO 1183 | 1.04 |
| 模具收缩率 | 流动 | ASTM D-955 | 0.4-0.6 | % |
| 拉伸模量 | | ISO 527-2/1 | 2600 | MPa |
| 抗张屈服强度 | | ASTM D-638 | 46.0 | MPa |
| | | ISO 527-2/50 | 50.0 |
| 断裂伸长率 | | ASTM D-638 | 15 | % |
| | | ISO 527-2/50 | 10 |
| 弯曲模量 | | ASTM D-790 | 2300 | MPa |
| 弯曲屈服强度 | | ASTM D-790 | 73.0 | MPa |
| | | ISO 178 | 77.0 |
| 简支梁缺口冲击强度 | 23℃ | ISO 179/1eA | 18 | KJ/m2 |
| 悬壁梁缺口冲击强度 | -30℃,3.20mm | ASTM D-256 | 108 | J/m |
| 悬壁梁缺口冲击强度 | -30℃,12.7mm | ASTM D-256 | 80.0 | J/m |
| 悬壁梁缺口冲击强度 | 0℃,3.20mm | ASTM D-256 | 157 | J/m |
| 悬壁梁缺口冲击强度 | ℃,12.7mm | ASTM D-256 | 108 | J/m |
| 悬壁梁缺口冲击强度 | 23℃,3.20mm | ASTM D-256 | 215 | J/m |
| 悬壁梁缺口冲击强度 | 23℃,12.7mm | ASTM D-256 | 196 | J/m |
| 洛氏硬度 | | ASTM D-785 | 114 | R-scale |
| 热变形温度 | 1.80MPa，未退火，6.40mm | ASTM D-648 | 86.0 | ℃ |
| | 1.80MPa，未退火，12.7mm | | 92.0 |
| | 1.80MPa，未退火 | ISO 75-2/A | 79.0 |
| 阻燃等级 | | UL94 | HB |
| 线形膨胀系数 | 流动 | ASTM D-696 | 0.000072 | cm/cm/℃ |
| 导热系数 | | ASTM C-177 | 0.15 | W/m/K |
| 表面电阻率 | | ASTM D-257 | 1.0E+16 | ohms |
| 体积电阻率 | 23℃ | ASTM D-257 | 1.0E+16 | ohm.cm |
| 介电强度 | | ASTM D-149 | 23 | KV/mm |
| 介电常数 | 1KHz | ASTM D-150 | 3.10 |
| 耗散因数 | 1KHz | ASTM D-150 | 0.0062 |