长供 供应热塑性弹性体TPE/TPR原料 轮子 美工刀 卷尺
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 24小时吸水率 | | ASTM D-570 | 0.6 | % |
| 泰伯磨耗量 | CS-17轮 | ASTM D-1044 | 3 | mg/1000rev |
| 比重 | | ASTM D-792 | 1.14 |
| 泰伯磨耗量 | H 18轮 | ASTM D-1044 | 72 | mg/1000rev |
| 熔体流动速率 | | ASTM D-1238 | 8.5 | g/10min |
| 初耐撕裂性能 | | ASTM D-1004 | 116 | kn/m |
| 拉伸力(5%伸长) | | ASTM D-638 | 4.1 | Mpa |
| 拉伸力(10%伸长) | | ASTM D-638 | 5.7 | Mpa |
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 不破裂 | J/m |
| 断裂伸长 | | ASTM D-638 | 600 | % |
| 揉曲模量 | 23℃ | ASTM D-790 | 94 | Mpa |
| 断裂拉伸力 | | ASTM D-638 | 31 | Mpa |
| 硬度计硬度 | | ASTM D-2240 | 45 |
| 熔点 | | ASTM D-3418 | 193 | ℃ |
| 维卡软化点 | | ASTM D-1525 | 158 | ℃ |
| 热畸变温度 | @0.18Mpa | ASTM D-648 | 43 | ℃ |
| 热畸变温度 | @0.5Mpa | ASTM D-648 | 60 | ℃ |
| 耐揉曲切口增长性能 | | ASTM D-1052 | >1×106 |