| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率190℃/2.16kgASTM D-123820g/10min |
| 熔体流动速率190℃/2.16kgISO 113320g/10min |
| 单体含量Internal Method9.7% |
| 物理性能比重ASTM D-7920.938g/cm3 |
| 比重ISO 11830.938g/cm3 |
| 机械性能拉伸屈服强度Compression MoldedASTM D-6387.24MPa |
| 拉伸屈服强度Compression MoldedISO 527-27.24MPa |
| 拉伸断裂强度Compression MoldedASTM D-63816.2MPa |
| 拉伸断裂强度Compression MoldedISO 527-216.2MPa |
| 拉伸断裂伸长率Compression MoldedASTM D-638580% |
| 拉伸断裂伸长率Compression MoldedISO 527-2580MPa |
| 加工性能熔体温度220-260℃ |
| 热性能维卡软化点ASTM D-152572.2℃ |
| 维卡软化点ISO 30672.2℃ |
| 熔融温度Internal Method95℃ |
| 其它性能密封起始温度Internal Method85℃ |
| 水汽传输速率38℃，90% RHDIN 53122/20.44g·mm/m2/atm/24hr |