韩国LG312C
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 成型收缩率 | | ASTM D-955 | 0.004-0.007 | mm/mm |
| 熔体流动速率 | 220℃/10kg | ASTM D-1238 | 60 | g/10min |
| 比重 | | ASTM D-792 | 1.20 |
| 弯曲弹性率 | | ASTM D-790 | 710 | kg/cm2 |
| 挠曲模量 | | ASTM D-790 | 24000 | kg/cm2 |
| 拉伸强度 | | ASTM D-638 | 430 | kg/cm2 |
| 洛氏硬度 | | ASTM D-785 | 100 | R-Scale |
| 延伸率 | | ASTM D-638 | 18 | % |
| 冲击强度 | Notched1/4" | ASTM D-256 | 18 | kgcm/cm |
| 抗弧光 | | ASTM D-495 | 7 | PLCCode |
| HWI | | UL-746A | 1 | PLCCode |
| CTI | | UL-746A | 1 | PLCCode |
| HVTR | | UL-746A | 2 | PLCCode |
| HAI | | UL-746A | 0 | PLCCode |
| 燃烧率 | 1/16" | IEC-707 | FV-0 | mm/min |
| 维卡软化点 | 1.000g | ASTM D-1525 | 85 | ℃ |
| 燃烧率 | 1/16" | UL-94 | V-0 |
| 热变形温度 | Unannealed18.5kg/cm1/2" | ASTM D-648 | 76 | ℃ |
| 燃烧率 | 1/8" | UL-94 | V-0 |