| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率220℃/10kgASTM D123811g/10min |
| 吸水率ASTM D5700.35% |
| 物理性能比重ASTM D7921.04g/cm3 |
| 模具收缩率ASTM D9550.4-0.6% |
| 机械性能拉伸强度ASTM D63845.1MPa |
| 断裂伸长率ASTM D63810% |
| 弯曲模量ASTM D7902550MPa |
| 弯曲强度ASTM D79074.5MPa |
| IZOD缺口冲击强度23℃,6.35mmASTM D256157J/m |
| 洛氏硬度ASTM D785114R-Scale |
| 热性能热变形温度1.8MPa,Unannealed,6.35mmASTM D64897℃ |
| 维卡软化点ASTM D1525108℃ |
| 阻燃等级1.59mm,ALLUL 94HB |