| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能吸水率23℃ASTM D-5700.23-0.26% |
| 熔体流动速率300℃，1.2kgISO Standard7.5-10.5g/10min |
| 物理性能比重ASTM D-7921.2 |
| 机械性能拉伸强度23℃ASTM D-63858.8-68.6(600-700)MPa(Kgf/cm2) |
| 弯曲模度23℃ASTM D-7902.3(2.3)GPa(104Kgf/cm2) |
| IZOD缺口冲击强度3.2mmASTM D-256740-1000(75-102）J/m(kg.cm/cm) |
| 洛氏硬度ASTM D-785R122-124(M60-70) |
| 挠曲强度23℃ASTM D-79080.4-90.2(820-920)MPa(Kgf/cm2) |
| 拉伸长度23℃ASTM D-63890-140% |
| 电气性能介电损耗正切106HzASTM D-1500.0082 |
| 表面电阻系数ASTM D-2571015 |
| 介电常数（电容率）106HzASTM D-15025.2(2.85)pF/m |
| 耐电压ASTM D-14918-22MV/m |
| 体积电阻系数ASTM D-2572.1×1016cm |
| 加工性能成形收缩率平行方向0.5-0.8% |
| 垂直方向0.5-0.8% |
| 热性能负荷挠曲温度455kPa(4.6Kgf/cm2)ASTM D-648136-142℃ |
| 燃烧性1.6mmUL 94HB |
| 线膨胀系数20℃-80℃ASTM D-6966-710-5·K-1 |
| 负荷挠曲温度820kPa(18.6Kgf/cm2)ASTM D-648130-136℃ |