供应 透明亚克力 聚甲基丙烯酸甲脂颗粒原料PMMA CM205
'
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 硬度 | | ASTM D-785 | M-95 | |
| 假密度 | | ASTM D-1182 | 0.77 | g/cm3 |
| 吸水率 | | ASTM D-570 | 0.3 | % |
| 物理性能 | 比重 | | ASTM D-792 | 1.19 | |
| 全光透过率 | | ASTM D-1003 | 92 | % |
| 流动系数 | | ASTM D-1238 | 1.8 | g/10min |
| 燃烧率 | | | 1/16"HB | UL-94 |
| 成型收缩率 | | ASTM D-955 | 0.002-0.006 | mm/mm |
| 机械性能 | 抗冲击力 | | ASTM D-256 | 2.0 | kg-cm/cm |
| 引张强度 | | ASTM D-638/PSI | 10200/720 | Kg/cm2 |
| 弯曲强度 | | ASTM D-790/PSI | 15600/1100 | Kg/cm2 |
| 延伸率 | | ASTM D-638 | 5.0 | % |
| 曲折率 | | ASTM D-542 | 1.491 | |
| 绝缘耐力 | | ASTM D-149 | 500 | Volts/Mil |
| 抗冲击力 | | ASTM D-256 | 0.37 | ft-lbs/in2 |
| 电气性能 | 体积固有抵抗 | | ASTM D-257 | 1015 | Ω.m |
| 失电率 | | ASTM D-150 | 0.19 | |
| 诱电率 | | ASTM D-150-647b | 3.7 | |
| 诱电率力 | | ASTM D-150-647 | 0.5 | |
| 热性能 | 热变形温度 | | ASTM D-648 | 100/212 | °C/°F |
| 维卡软化点 | | ASTM D-648 | 113/235 | °C/°F |