| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能熔体流动速率200℃/5kgASTM D-12384.0g/10min |
| 模具收缩率FlowASTM D-9550.30-0.60% |
| 吸水率24hrASTM D-5700.050% |
| 物理性能比重ASTM D-7921.04g/cm3 |
| 机械性能拉伸屈服强度ASTM D-63840.1MPa |
| 拉伸屈服伸长率ASTM D-63845% |
| 弯曲模量ASTM D-7902250MPa |
| 弯曲屈服强度ASTM D-79043.1MPa |
| IZOD缺口冲击强度3.18mmASTM D-25689.1J/m |
| 洛氏硬度ASTM D-78580L scale |
| 电气性能体积电阻率ASTM D-2571.0E+16ohm.cm |
| 介电强度ASTM D-14917.7KV/mm |
| 介电常数1E+6HzASTM D-1502.700 |
| 热性能热变形温度1.80MPa，未退火ASTM D-64882.2℃ |
| 维卡软化温度ASTM D-1525101℃ |
| 燃烧性1.59mmUL 94HB |
| 燃烧性3.18mmUL 94HB |
| 燃烧性6.35mmUL 94HB |
| RTI Str1.59mmUL 74650.0℃ |
| RTI Str3.18mmUL 74650.0℃ |
| RTI Str6.35mmUL 74650.0℃ |
| RTI Imp1.59mmUL 74650.0℃ |
| RTI Imp3.18mmUL 74650.0℃ |
| RTI Imp6.35mmUL 74650.0℃ |
| RTI Elec1.59mmUL 74650.0℃ |
| RTI Elec3.18mmUL 74650.0℃ |
| RTI Elec6.35mmUL 74650.0℃ |