PC-1100韩国湖南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
物理性能 | 流动性 | | ASTM D1238 | 10 | g/10min |
密度 | | ASTM D792 | 1.2 | |
模塑收缩率 | | ASTM D955 | 0.5-0.7 | % |
吸水率 | | ASTM D570 | 0.2 | % |
机械性能 | 拉伸强度 | | ASTM D638 | 630 | kg/cm2 |
伸长率 | | ASTM D638 | 110 | % |
弯曲强度 | | ASTM D790 | 920 | kg/cm2 |
弯曲模量 | | ASTM D790 | 24000 | kg/cm2 |
洛氏硬度 | | ASTM D785 | 77 | M |
缺口冲击强度 | | ASTM D256 | 87 | kg.cm/cm |
电气性能 | 体积电阻率 | 1016 | ASTM D257 | 3 | Ω.cm |
损耗因数 | | ASTM D150 | 2.95 | |
热性能 | 热变形温度 | - | 1.8Mpa | ASTM D648 | 125 | ℃ |
- | 0.45Mpa | ASTM D648 | 136 | ℃ |
线膨胀系数 | | ASTM D696 | 6-8 | |
维卡软化温度 | | ASTM D1525 | 153 | ℃ |
光学性能 | 透光率 | | ASTM D1003 | 89 | % |
雾度 | | ASTM D1003 | <0.8 | % |
折射率 | | ASTM D542 | 1.585 |