抗冲 日本东丽 ABS 700-314
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 吸水性 | 23℃×24小时 | ASTM D-570 | 0.3 | % |
| 流动系数 | 220℃ 10kg(98N) | ASTM D-1238 | 23 | g/10min |
| 比重 | | ASTM D-792 | 1.05 | g/cm3 |
| 模具收缩率 | | Tory Method | 0.40-0.60 | % |
| 引张强度 | | ASTM D-638 | 510(50) | kg/cm2(MPa) |
| 延伸率 | 23℃ | ASTM D-638 | 35 | % |
| 弯曲强度 | 23℃ | ASTM D-790 | 770(76) | kg/cm2(MPa) |
| 弯曲弹性率 | 23℃ | ASTM D-790 | 25000(-2450) | kg.cm/cm(MPa) |
| 冲击强度 | 23℃ | ASTM D-256 | 19(186) | kg.cm/cm(J/m) |
| 冲击强度 | 0℃ | ASTM D-256 | 11(108) | kg.cm/cm(J/m) |
| 冲击强度 | -30℃ | ASTM D-256 | 8(78) | kg.cm/cm(J/m) |
| 洛氏硬度 | | ASTM D-785 | 115 | R scale |
| 表面电阻指数 | 23℃ | ASTM D-257 | >1016 | ohm |
| 体积电阻指数 | 23℃ | ASTM D-257 | >1016 | ohm.cm |
| 绝缘耐力 | 短时间 | ASTM D-194 | 23 | KV/mm |
| 诱电指数 | 1000Hz | ASTM D-150 | 3.1 |
| 热变形温度 | 18.56kg/cm2(1.82MPa) | ASTM D-648 | 92 | ℃ |
| 线膨胀系数 | | ASTM D-696 | 7.1×10-5 | mm/mm℃ |
| 热导指数 | | ASTM C-177 | 0.15 | W/K.m |
| 燃烧性 | | UL 94 | HB |