供应美国埃克森美孚EVA Ultra LD 705.MJ blown
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 熔流率 | 190°C/2.16 kg | ASTM D1238 | 0.40 | g/10 min |
| 醋酸乙烯含量 | | ExxonMobil Method | 12.8 | wt% |
| 机械性能 | 割线模量 | 1% 正割, MD | ASTM D882 | 80.4 | MPa |
| | 1% 正割, TD | ASTM D882 | 89.9 | MPa |
| 抗张强度 | MD: 断裂 | ASTM D882 | 33.9 | MPa |
| | TD: 断裂 | ASTM D882 | 34.6 | MPa |
| 伸长率 | MD: 断裂 | ASTM D882 | 360 | % |
| | TD: 断裂 | ASTM D882 | 660 | % |
| 落锤冲击 | | ASTM D1709A | 710 | g |
| 埃尔曼多夫抗撕强度 | MD | ASTM D1922 | 66 | g |
| | | TD | ASTM D1922 | 82 | g |
| 热性能 | 维卡软化温度 | | ASTM D1525 | 76.0 | °C |