PC LV-2250Y日本帝人 冰色、易脱模型防火
①原料描述部分| 规格级别 | 注塑 | 外观颜色 | |
| 该料用途 | |
| 备注说明 | 类型：冰色、易脱模型 |
③原料技术数据
| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能吸水率24hr，in 23℃ASTM D-5700.20% |
| 物理性能折射率ASTM D-5421585 |
| 透光率3mm thickASTM D-100388 |
| 阻燃性0.38mmUL 94V-2 |
| 比重JIS K-71121.20 |
| 机械性能拉伸模量ASTM D-6382120(21600)Mpa(kgf/cm2) |
| 弯曲模量ASTM D-7902230(22700)Mpa(kgf/cm2) |
| 拉伸率屈服点ASTM D-6386% |
| 断裂点ASTM D-638140% |
| 弯曲强度ASTM D-79090(915)Mpa(kgf/cm2) |
| 耐冲击强度值艾氏、带缺口厚度3.2mmASTM D-256880(90)J/m(kgf·cm/cm) |
| 压缩强度ASTM D-69576(770)Mpa(kgf/cm2) |
| 洛氏硬度ASTM D-78577M标度 |
| 耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-256140(14)J/m(kgf·cm/cm) |
| 拉伸强度屈服点ASTM D-63861(620)Mpa(kgf/cm2) |
| 断裂点ASTM D-63881(830)Mpa(kgf/cm2) |
| 电气性能介电率60HzASTM D-1502.95 |
| 耐电弧性ASTM D-495110sec |
| 介电正切106HzASTM D-1500.009 |
| 绝缘破坏强度快速加压值厚度1.6mmASTM D-14930kv/mm |
| 介电正切60HzASTM D-1500.0004 |
| 介电率106HzASTM D-1502.9 |
| 耐导电径迹性（CTI）IEC 112300V |
| 体积电阻率ASTM D-2573×1016Ω.cm |
| 加工性能成型收缩率流动方向ASTM D-9550.5～0.7% |
| 垂直方向ASTM D-9550.5～0.7% |
| 热性能温度指数电学式厚度1.47mmUL 746B125℃ |
| 冲击式厚度1.47mmUL 746B115℃ |
| 非冲击式厚度1.47mmUL 746B125℃ |
| 线膨胀系数流动方向ASTM D-696710-5cm/cm/℃ |
| 垂直方向ASTM D-696710-5cm/cm/℃ |
| 负荷挠曲温度负荷1.813MPa(18.6kgf/cm2)JIS K-7207133℃ |
| 负荷挠曲温度负荷0.451MPa(4.6kgf/cm2)JIS K-7207143℃ |