Shinko-Lac ABS GH-8 Mitsubishi Rayon America Inc. ABS
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 200℃/5.0kg | ASTM D-1238 | 1.2 | g/10min |
| 吸水率 | 24hr | ASTM D-570 | 0.30 | % |
| 比重 | | ASTM D-792 | 1.04 | g/cm3 |
| 模具收缩率 | Flow | ASTM D-955 | 0.50 | % |
| 洛氏硬度 | | ASTM D-785 | 94 | R-Scale |
| 拉伸模量 | 23℃ | ASTM D-638 | 1860 | MPa |
| 拉伸屈服强度 | 23℃ | ASTM D-638 | 35.3 | MPa |
| 弯曲模量 | 23℃，6.35mm | ASTM D-790 | 1860 | MPa |
| 弯曲屈服强度 | 23℃，6.35mm | ASTM D-790 | 53.0 | MPa |
| IZOD缺口冲击强度 | -40℃，6.35mm | ASTM D-256 | 147 | J/m |
| IZOD缺口冲击强度 | 0℃，6.35mm | ASTM D-256 | 284 | J/m |
| IZOD缺口冲击强度 | 23℃，6.35mm | ASTM D-256 | 373 | J/m |
| 热变形温度 | 1.80MPa，未退火，12.7mm | ASTM D-648 | 89.0 | ℃ |
| CLTE | Flow | ASTM D-696 | 0.000095 | cm/cm/℃ |
| 比热 | | ASTM C-351 | 1670 | J/kg/℃ |
| 导热系数 | | ASTM C-177 | 0.21 | W/m.K |
| UL档案号 | | | E54695 |