熔体流动速率:5.5 g/10min|密度:1.165 g/cm3|吸水率:0.4 %|成型收缩率:0.4 - 0.8 %|缺口冲击强度:4.5|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 吸水率 | 24h | ASTM D-570 | 0.4 | % |
| 物理性能 | 反射指数 | | ASTM D-542 | 1.49 | |
| 比重 | | ASTM D-792 | 1.165 | |
| 透明性 | 3.2mm | ASTM D-1003 | 91 | % |
| 机械性能 | 延伸率 | | ASTM D-638 | 30 | % |
| 冲击强度 | Izod Notched | ASTM D-256 | 4.5 | kg·cm/cm2 |
| 弯曲模数 | | ASTM D-790 | 23,000 | Kg/cm2 |
| 弯曲强度 | | ASTM D-790 | 900 | Kg/cm2 |
| 洛氏硬度 | M-Scale | ASTM D-785 | 60 | |
| 拉力 | | ASTM D-638 | 500 | Kg/cm2 |
| 电气性能 | 介电强度 | 4KV/S | ASTM D-149 | 15 | KV/mm |
| 介电定数 | 60Hz | ASTM D-150 | 3.9 | |
| 抗体积系数 | | ASTM D-257 | >1515 | Ω.m |
| 功率系数 | 60Hz | ASTM D-150 | 0.04 | |
| 热性能 | 比热 | cal/g/°C | | 0.35 | |
| 模缩系数 | | ASTM D995-51 | 0.4-0.8 | % |
| 维卡软化点 | 1kg | ASTM D-1525 | 90 | °C |
| 绵性膨胀系数 | cm/cm/°C | ASTM D-696 | 6×10-5 | |
| 流动指数 | 230°C,3.8kg | ASTM D-1238 | 5.5 | g/10min |
| 热传导 | | ASTM D-177 | 5×10-4 | cal/seccm·°C/cm |
| 燃烧度 | 1/8",1/16" | UL94 | HB | |
| 热变形温度 | 18.56kg | ASTM D-648 | 88 | °C |