阻燃等级,V-0级ABS884 X01日本东丽 ABS 日本东丽 884
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 200℃/5.0kg | ISO 1133 | 5.0 | g/10min |
| 比重 | | ASTM D-792 | 1.15 | g/cm3 |
| | | ISO 1183 | 1.16 |
| 模具收缩率 | 流动 | ASTM D-955 | 0.4-0.7 | % |
| 拉伸模量 | | ISO 527-2/1 | 2700 | MPa |
| 抗张屈服强度 | | ASTM D-638 | 45.0 | MPa |
| | | ISO 527-2/50 | 49.0 |
| 断裂伸长率 | | ASTM D-638 | 5.0 | % |
| | | ISO 527-2/50 | 5.0 |
| 弯曲模量 | | ASTM D-790 | 2310 | MPa |
| 弯曲屈服强度 | | ASTM D-790 | 70.0 | MPa |
| | | ISO 178 | 68.0 |
| 简支梁缺口冲击强度 | 23℃ | ISO 179/1eA | 14 | KJ/m2 |
| 悬壁梁缺口冲击强度 | 3.20mm | ASTM D-256 | 245 | J/m |
| 悬壁梁缺口冲击强度 | 12.7mm | ASTM D-256 | 157 | J/m |
| 洛氏硬度 | | ASTM D-785 | 104 | R-scale |
| 热变形温度 | 1.80MPa，未退火，6.40mm | ASTM D-648 | 76.0 | ℃ |
| | 1.80MPa，未退火 | ISO 75-2/A | 70.0 |
| 阻燃等级 | 0.750mm | UL94 | V-2 |
| 阻燃等级 | 1.50mm | UL94 | V-0 |
| 阻燃等级 | 2.50mm | UL94 | 5VA |