产品参数性能项目试验条件[状态]测试方法测试数据数据单位挠曲系数23℃ASTM D-7903220MPa模收缩
2.2-2.4%吸水量浸渍平衡点ASTM D-5700.90%吸水量50%相对湿度ASTM D-5700.22%比重 ASTM D-7921.42吸水量24小时浸渍ASTM D-5700.25%拉伸强度100℃ASTM D-63836MPa抗剪强度23℃ASTM D-73266MPa压缩应力23℃ 10%变形ASTM D-695121MPa抗拉伸冲击强度长试片23℃ASTM D-1822250KJ/m2拉伸强度23℃ASTM D-63869MPa破裂点拉伸变形量70℃ASTM D-638180%挠曲疲劳忍耐限度50%RH 23℃ 106周期ASTM D-67132MPa弹性系数23℃ASTM D-6383640MPaIZOD冲击强度缺口-40℃ASTM D-25655J/m负载变形量140kg/cm2 50℃ASTM D-6210.5%拉伸强度-55℃ASTM D-638101MPa挠曲系数100℃ASTM D-7901030MPa压缩应力23℃ 1%变形ASTM D-69535MPa拉伸强度122℃ASTM D-63826MPa洛氏硬度R ASTM D-785120IZOD冲击强度23℃ASTM D-25671J/m挠曲系数70℃ASTM D-7901720MPa洛氏硬度M ASTM D-78594挠曲系数-55℃ASTM D-7904730MPa挠曲变形强度23℃ASTM D-79097MPa破裂点拉伸变形量100℃ASTM D-638>260%IZOD冲击强度无缺口23℃ASTM D-2561620J/m拉伸强度70℃ASTM D-63848MPa破裂点拉伸变形量23℃ASTM D-63825%破裂点拉伸变形量122℃ASTM D-638>260%破裂点拉伸变形量-55℃ASTM D-63810%挠曲系数122℃ASTM D-790755MPa抗电弧3.1mmASTM D-495220sec容积电阻率23℃ 0.2%含水量ASTM D-2571015Ω .cm介电常数50%RH 23℃ 102～106HzASTM D-1503.7Ω .cm介电因数50%RH 23℃ 106HzASTM D-1500.005介电强度瞬间Short time(2.3mm)ASTM D-14919.7kv/mm熔点℃ASTM D-2133175℃自燃性 UL 94HB线性热膨胀系数29～60℃ASTM D-69612.210-5m/m℃热畸变温度1.8MPaASTM D-648136℃线性热膨胀系数60～104℃ASTM D-69613.710-5m/m℃热传导系数 0.37W/mk线性热膨胀系数-40～29℃ASTM D-69610.410-5m/m℃线性热膨胀系数104～160℃ASTM D-69614.910-5m/m℃热畸变温度0.5MPaASTM D-648172℃POM(聚甲醛)911P/美国杜邦注塑生产厂商：美国杜邦公司特性备注：加工特性：高流动性低黏度表面经润滑树脂，DELRIN 900P有优异的成型特性。产品与DELRIN 500相近，但稍微低的拉伸延伸率和冲击强度。收缩率低，耐燃油，热定性相同delrinp，成型周期缩短5%-15%，机械性能好，尺寸稳定性更好，耐疲劳，耐蠕变，刚性等都优于共聚甲千，综合了？用途：较多模穴与较不易填充的薄肉成型品。适合工程制品，由于结晶度的提高，又降低了薄壁制品产生孔隙的危险。重要参数：密度:1.42 g/cm3吸水率:0.25 %成型收缩率:2.3 %缺口冲击强度:55拉伸强度:69 MPa