性能项目
试验条件[状态]
测试方法
测试数据
数据单位
| 熔体流动速率 |
200℃,5000g |
ASTM D-1238 |
4.6 |
g/10min |
| 比重 |
23℃(73H) |
ASTM D-792 |
1.19 |
|
| 弯曲强度 |
1/8"×1"×4"bar 15mm/min 23℃(73H) |
ASTM D-790 |
715(70.1)(10.17) |
kgf/cm2(MPa)(PSI×103) |
| 拉伸强度 |
1/8" 50mm/min 23℃(73H) |
ASTM D-638 |
435(42.6)(6.19) |
kgf/cm2(MPa)(PSI×103) |
| 弯曲械量 |
1/8"×1"×4"bar 15mm/min 23℃(73H) |
ASTM D-790 |
24000(2.35)(3.41) |
kgf/cm2(GPa)(PSI×103) |
| IZOD冲击强度 |
1/4" 6.35mm 23℃(73H) |
ASTM D-256 |
20(196)(3.67) |
kgf.cm/cm(J/m)(Ft-lbs/in) |
| 洛氏硬度 |
23℃(73H) |
ASTM D-785 |
102 |
R Scale |
| UL燃烧等级 |
file NO:E206417 C-UL CSA LS 103112 1/16 |
UL 94 |
5VA |
|
| 热变形温度 |
1/2"×1/2"×5"bar 18.6kg/cm2(264PSI) |
ASTM D-648 |
78(172) |
℃(H) |
| UL燃烧等级 |
file NO:E206417 C-UL CSA LS 103112 1/8 |
UL 94 |
5VA |