原料用途及物性
LDPE/6130F/台湾塑胶
LDPE/6130F/台湾塑胶描述部分 |
规格级别 | 其它 其它 其它 | 外观颜色 | |
该料用途 | 收缩膜、积压膜、中空吹制。 |
备注说明 | 特性：收缩性优、光学优良、刚性适中。 |
LDPE/6130F/台湾塑胶技术数据
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
基本性能 | 密度 | | ASTM D-1505 | 0.924 | g/cm3 |
熔体流动速率 | | ASTM D-1238 | 0.8 | g/10min |
机械性能 | 抗撕裂性 | MD | | ASTM D-1922 | 45 | N/mm |
TD | | ASTM D-1922 | 60 | N/mm |
拉力降伏强度 | MD | | ASTM D-882B | 100 | kg/cm2 |
TD | | ASTM D-882B | 110 | kg/cm2 |
拉力降伏强度 | | ASTM D-638 | 120 | kg/cm2 |
拉力断裂强度 | | ASTM D-638 | 170 | kg/cm2 |
硬度 | | ASTM D-2240 | 54 | Shore D |
摩擦系数 | | ASTM D-1894 | >0.5 | |
落球行动强度 | | ASTM D-1709 | 260 | g |
弯曲模量 | | ASTM D-790 | 1800 | kg/cm2 |
拉力断裂伸长率 | | ASTM D-638 | 700 | % |
拉力断裂伸长率 | MD | | ASTM D-882B | 380 | % |
TD | | ASTM D-882B | 600 | % |
1%伸长弹性系数 | MD | | ASTM D-882B | 1900 | kg/cm2 |
TD | | ASTM D-882B | 2150 | kg/cm2 |
拉力断裂强度 | MD | | ASTM D-882B | 220 | kg/cm2 |
TD | | ASTM D-882B | 190 | kg/cm2 |
热性能 | 软化点 | | ASTM D-1525 | 98 | ℃ |
熔点 | | DSC | 113 | ℃ |
脆化温度 | | ASTM D-746 | <-70 | ℃ |
LDPE 台湾塑胶 6130F 适用于收缩膜 LDPE 台湾塑胶 6130F 适用于薄膜
提供SONY认证 SGS认证 ROHS报告 FDA认证等，欢迎来电洽谈！
LDPE 低密度聚乙烯的特性
化学和物理特性：
商业用的LDPE 材料的密度为0.91~0.94 g/cm3。LDPE 对气体和水蒸汽具有渗透性。
LDPE 的热膨胀系数很高不适合于加工长期使用的制品。
如果 LDPE 的密度在0.91~0.925 g/cm3 之间，那么其收缩率在2%~5%之间；如果密度在0.926~0.94 g/cm3 之间，那么其收缩率在1.5%~4%之间。当前实际的收缩率还要取决于注塑工艺参数。LDPE 在室温下可以抵抗多种溶剂，但是芳香烃和氯化烃溶剂可使其膨胀。同HDPE类似，LDPE 容易发生环境应力开裂现象。
注塑模工艺条件：
干燥：一般不需要
熔化温度：180~280C
模具温度：20~40C为了实现冷却均匀以及较为经济的去热，建议冷却腔道直径至少为8mm，并且从冷却腔
道到模具表面的距离不要超过冷却腔道直径的1.5 倍。
注射压力：最大可到1500bar。
保压压力：最大可到750bar。
注射速度：建议使用快速注射速度。
流道和浇口:可以使用各种类型的流道和浇口。LDPE特别适合于使用热流道模具。
典型用途：碗，箱柜，管道联接器，日用品。