ltems

Method

Units

PPS

Thermal conductivity through plane(层间导热系数)

ASTM1461-07

W/m-k

2

Thermal conductivity in plane(层内导热系数)

18

Flame rerardancy(阻燃性)

UL94

1.8mm

VO

Volume Resistivity(体积电阻)

D257

Ωcm

<10000

Mold shrinkage(注塑收缩率)

D955

%

0.3-0.7

Specific Gravity(比重)

D792

g/cm3

1.62

Melt Flow Rate(熔融指数)

D1238

g/10min

/

Tesnile Strength(拉伸强度)

D638

Mpa

64

Elongation at Break(断裂伸长率)

D638

%

<0.5

Flexural Strength(弯曲强度)

D790

Mpa

101

Flexural Modulus(弯曲模量)

D790

Mpa

10020

Izod Impact(悬臂梁冲击强度)

J/M

3.6

N-Chrpy Impact(简支梁冲击强度)

ISO 179/1eA

KJ/m2

/