ABS/韩国锦湖/HFA707阻燃耐化学性高光泽、高耐冲击
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 200℃/21.6kg | ASTM D-1238 | 120 | g/10min |
| 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 6.0 | g/10min |
| 熔体流动速率 | 220℃/10.0kg | ASTM D-1238 | 60 | g/10min |
| 吸水率 | 24hr | ASTM D-570 | 0.30 | % |
| 物理性能 | 比重 | | ASTM D-792 | 1.18 | g/cm3 |
| 模具收缩率 | Flow | ASTM D-955 | 0.40-0.70 | % |
| 机械性能 | 拉伸屈服强度 | 23℃ | ASTM D-638 | 44.1 | MPa |
| 拉伸屈服伸长率 | 23℃ | ASTM D-638 | 40 | % |
| 弯曲模量 | 23℃ | ASTM D-790 | 2060 | MPa |
| 弯曲屈服强度 | 23℃ | ASTM D-790 | 58.8 | MPa |
| IZOD缺口冲击强度 | 23℃,3.20mm | ASTM D-256 | 235 | J/m |
| IZOD缺口冲击强度 | 23℃,6.40mm | ASTM D-256 | 219 | J/m |
| 洛氏硬度 | | ASTM D-785 | 100 | R scale |
| 热性能 | 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 76.1 | ℃ |
| 维卡软化温度 | | ASTM D-1525 | 91.1 | ℃ |
| 燃烧性 | 1.50mm | UL 94 | V-0 | |
| 燃烧性 | 3.00mm | UL 94 | V-0 | |