日本出光石油化学Idemitsu HIPS HT50
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 4.0 | g/10min |
| 吸水率 | | ASTM D-570 | <0.1 | % |
| 物理性能 | 比重 | | ASTM D-792 | 1.04 | |
| 模具收缩率 | | ASTM D-955 | 0.004-0.007 | cm/cm |
| 机械性能 | 拉伸断裂强度 | | ASTM D-638 | 310 | Kg/cm2 |
| 拉伸断裂伸长率 | | ASTM D-638 | 40 | % |
| 弯曲强度 | | ASTM D-790 | 560 | Kg/cm2 |
| 弯曲模量 | | ASTM D-790 | 22000 | Kg/cm2 |
| IZOD缺口冲击强度 | | ASTM D-256 | 8.5 | kg.cm/cm |
| 洛氏硬度 | | ASTM D-785 | L60 | L scale |
| 线膨胀系数 | | ASTM D-696 | 5-10 | *10-5mm/mm/℃ |
| 热性能 | 热变形温度 | | ASTM D-648 | 85 | ℃ |
| 维卡软化点 | | ASTM D-1525 | 107 | ℃ |
| 燃烧性 | | UL 94 | HB | Flame Class |
| HWI | | UL 746A | 4 | HWI PLC |
| HAI | | UL 746A | 0 | HAI PLC |
| 电气RTI | | UL 764B | 50 | ℃ |
| 机械冲击RTI | | UL 764B | 50 | ℃ |
| 机械强度RTI | | UL 764B | 50 | ℃ |