EVA/台湾聚合/UE629
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 其它性能 | 射出 | | ASTM D-638/D-882 | 220 | % |
| 铸膜成型 | | ASTM D-638/D-882 | 750 | % |
| 薄膜 | MD | | ASTM D-638/D-882 | 250 | kg/cm2 |
| TD | | ASTM D-638/D-882 | 240 | kg/cm2 |
| 薄膜 | MD | | ASTM D-638/D-882 | 480 | % |
| TD | | ASTM D-638/D-882 | 640 | % |
| 机械性能 | 冲击强度 | | ASTM D-1709 | 430 | G/F50 |
| 其它性能 | 射出 | | ASTM D-638/D-882 | 117 | kg/cm2 |
| VA含量 | | ASTM USIFE | 18 | % |
| 密度 | | ASTM D-1505 | 0.939 | g/cm3 |
| 融化点 | | ASTM D-2117 | 86 | ℃ |
| VICAT 软化点 | | ASTM D-1525 | 64 | ℃ |
| 熔融指数 | | ASTM D-1238 | 2.5 | g/10min |
| 低温易脆性 | | ASTM D-746 | <-76 | ℃/F50 |
| 硬度 | | ASTM D-2240 | 31 | Shore D |
| 铸膜成型 | | ASTM D-638/D-882 | 180 | kg/cm2 |