| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 吸水率 | 24hr | ASTM D-570 | DAM｜50%RH,0.5｜- | % |
| 比重 | ASTM D-792DAM｜50%RH,1.56｜- |
| 模具收缩率 | 3.2mm flow | ASTM D-792 | DAM｜50%RH,0.4｜- | % |
| 弯曲强度 | ASTM D-790DAM｜50%RH,240｜-MPa |
| 断裂伸长率 | ASTM D-638DAM｜50%RH,2.5｜4% |
| IZOD缺口冲击强度 | ASTM D-256DAM｜50%RH,100｜105J/m |
| 弯曲模量 | ASTM D-790DAM｜50%RH,8960｜6900MPa |
| 拉伸强度 | ASTM D-638DAM｜50%RH,169｜134MPa |
| 体积电阻率 | ASTM D-257DAM｜50%RH,10,14,｜10,11Ω.cm |
| 损耗因数 | 103Hz | ASTM D-150 | DAM｜50%RH,DAM｜50%RH,0.｜541,0.009｜0.113 |
| 介电常数 | 103Hz | ASTM D-150 | DAM｜50%RH,3.6｜5.1 |
| 表面电阻率 | ASTM D-257DAM｜50%RH,10,14,｜10,11Ω |
| 介电强度 | 3.2mm | ASTM D-149 | DAM｜50%RH,17.2｜15.6 | kv/mm |
| 损耗因数 | 106Hz | ASTM D-150 | DAM｜50%RH,0.014｜0.041 |
| 介电常数 | 106Hz | ASTM D-150 | DAM｜50%RH,3.5｜3.8 |
| 热变形温度 | 0.45MPa | ASMT D-648 | DAM｜50%RH,257｜- | ℃ |
| 热变形温度 | 1.80MPa | ASTM D-648 | DAM｜50%RH,235｜- | MPa |
| 熔点 | ASTM D-3418DAM｜50%RH,262｜-℃ |