ABS/韩国锦湖/HFA-462HT 挤出级ABS ABS耐老化挤出 V0阻燃ABS
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 200℃/21.6kg | ASTM D-1238 | 32 | g/10min |
| 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 1.6 | g/10min |
| 熔体流动速率 | 220℃/10.0kg | ASTM D-1238 | 16 | g/10min |
| 吸水率 | 24hr | ASTM D-570 | 0.30 | % |
| 物理性能 | 比重 | | ASTM D-792 | 1.18 | g/cm3 |
| 模具收缩率 | Flow | ASTM D-955 | 0.40-0.70 | % |
| 机械性能 | 拉伸屈服强度 | 23℃ | ASTM D-638 | 51.0 | MPa |
| 拉伸屈服伸长率 | 23℃ | ASTM D-638 | 25 | % |
| 弯曲模量 | 23℃ | ASTM D-790 | 2260 | MPa |
| 弯曲屈服强度 | 23℃ | ASTM D-790 | 61.8 | MPa |
| IZOD缺口冲击强度 | 23℃,3.20mm | ASTM D-256 | 219 | J/m |
| IZO缺口冲击强度 | 23℃,6.40mm | ASTM D-256 | 198 | J/m |
| 洛氏硬度 | | ASTM D-785 | 105 | R scale |
| 热性能 | 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 80.0 | ℃ |
| 维卡软化温度 | | ASTM D-1525 | 96.1 | ℃ |
| 燃烧性 | 1.50mm | UL 94 | V-0 | |