MECHANICAL

Tensile Stress, yld, Type I, 5 mm/min

420

kgf/cm²

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min

320

kgf/cm²

ASTM D 638

Tensile Strain, yld, Type I, 5 mm/min

2.1

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

26

%

ASTM D 638

Tensile Modulus, 5 mm/min

21000

kgf/cm²

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

690

kgf/cm²

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

21700

kgf/cm²

ASTM D 790

IMPACT

Izod Impact, notched, 23°C

35

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

316

cm-kgf

ASTM D 3763

THERMAL

Vicat Softening Temp, Rate B/50

98

°C

ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed

97

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed

82

°C

ASTM D 648

CTE, -40°C to 40°C, flow

8.82E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

8.64E-05

1/°C

ASTM E 831

Relative Temp Index, Elec

60

°C

UL 746B

Relative Temp Index, Mech w/impact

60

°C

UL 746B

Relative Temp Index, Mech w/o impact

60

°C

UL 746B

PHYSICAL

Specific Gravity

1.05

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.5 - 0.8

%

SABIC Method

Melt Flow Rate, 230°C/3.8 kgf

3.7

g/10 min

ASTM D 1238

Melt Viscosity, 240°C, 1000 sec-1

2450

poise

ASTM D 3825

Melt Volume Rate, MVR at 220°C/10.0 kg

15

cm³/10 min

ISO 1133

ELECTRICAL

Arc Resistance, Tungsten {PLC}

5

PLC Code

ASTM D 495

Hot Wire Ignition {PLC)

3

PLC Code

UL 746A

High Voltage Arc Track Rate {PLC}

2

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC}

0

PLC Code

UL 746A

Comparative Tracking Index (UL) {PLC}

0

PLC Code

UL 746A

FLAME CHARACTERISTICS

UL Recognized, 94HB Flame Class Rating (3)

1.52

mm

UL 94

Injection Molding

Drying Temperature

80 - 95

°C

Drying Time

2 - 4

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0.1

%

Melt Temperature

220 - 260

°C

Nozzle Temperature

220 - 260

°C

Front - Zone 3 Temperature

215 - 240

°C

Middle - Zone 2 Temperature

205 - 225

°C

Rear - Zone 1 Temperature

190 - 210

°C

Mold Temperature

50 - 70

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

30 - 60

rpm

Shot to Cylinder Size

50 - 70

%

Vent Depth

0.038 - 0.051

mm