该类不锈钢焊丝均符合国家冶金工业部弹簧焊丝推荐标准。
材质 | 用途 | 化学成分 | 力学能力 | 线径（mm） | 净重(kg) | 阀芯直径(mm) | 备注 |
ER304 | 主要用于焊接18Cr-8Ni钢 | C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% | 拉伸强度Mpa 1200 | 0.08-0.45 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER304L | 主要用于焊接17Cr-8Ni钢 | C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER308 | 主要用于焊接19Cr-9Ni钢 | C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER308L | 主要用于焊接20Cr-9Ni钢 | C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10% | 拉伸强度Mpa 1200 | 0.8-4.5 | 5/12.5/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER309 | 主要用于焊接20Cr-13Ni钢 | C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER309L | 主要用于焊接20Cr-14Ni钢 | C:0.024% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER309Lsi | 主要用于焊接20Cr-14Ni钢 | C:0.024% Mn:1.65% Si:1.02% Ni:14.33% Cr:20.10% | 拉伸强度Mpa1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER321 | 主要用于焊接16Cr-7Ni钢 | C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10%Ti0.73 | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER347 | 主要用于焊接16Cr-9Ni钢 | C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% （Ta+Nb）（10*C）-10 | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 0 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER347L | 主要用于焊接17Cr-9Ni钢 | C:0.064% Mn:1.65% Si:0.42% Ni:9.33% Cr:17.10% （Ta+Nb）（10*C）-10 | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 0 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER316 | 主要用于焊接16Cr-9Ni钢 | C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03 | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER316L | 主要用于焊接17Cr-9Ni钢 | C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:17.10% Mo2.03 | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |
ER310 | 主要用于焊接24Cr-19Ni钢 | C:0.064% Mn:1.65% Si:0.42% Ni:20.33% Cr:25.10% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 TIG:1.0-4.5 |