非氯化、非溴化PPO N225X 沙伯基础(原GE) 品牌
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 模塑收缩量, flow, 0.125" | | ASTM D-955 | 5-7 | in/in E-3 |
| 模塑收缩量, xflow, 0.125" | | ASTM D-955 | 5-7 | in/in E-3 |
| 比重, 固体 | | ASTM D-792 | 1.11 | |
| 机械性能 | 仪表控制抗冲击能量 @ 峰值, -22F. | | ASTM D-3763 | 8.6 | ft-lbs |
| 拉伸伸长, 断裂, 类型 I 0.125" | | ASTM D-638 | 17.0 | % |
| 伊佐德冲击值, 反向缺口, -22F | | ASTM D-256 | 12.0 | ft-lb/in |
| 抗拉强度, 屈服, 类型 I, 0.125" | | ASTM D-638 | 9700 | psi |
| 伊佐德冲击值, 缺口, 73F | | ASTM D-256 | 3.5 | ft-lb/in |
| 挠曲强度, 屈服, 0.250 | | ASTM D-790 | 14400 | psi |
| 伊佐德冲击值, 缺口, -22F | | ASTM D-256 | 1.8 | ft-lb/in |
| 挠曲模量, 0.250" | | ASTM D-790 | 361500 | psi |
| 拉伸伸长, 屈服, 类型 I 0.125" | | ASTM D-638 | 8.0 | % |
| 伊佐德冲击值, 反向缺口, 73F | | ASTM D 256 | 16.6 | ft-lb/in |
| 仪表控制抗冲击能量 @ 峰值, 73F. | | ASTM D-3763 | 29.0 | ft-lbs |
| 抗拉强度, 断裂, 类型 I, 0.125" | | ASTM D 638 | 7200 | psi |
| 电气性能 | 体积电阻率 | | ASTM D-257 | 2 E16 | ohm-cm |
| 介电常数, 50 Hz | | ASTM D-150 | 2.69 | |
| 损耗因数, 1 MHz | | ASTM D-150 | 0.0070 | |
| 介电强度, 油内, 125 mils | | ASTM D-149 | 414 | V/mil |
| 介电常数, 1 MHz | | ASTM D-150 | 2.55 | |
| 损耗因数, 50 Hz | | ASTM D-150 | 0.0100 | |
| 表面电阻率 | | ASTM D-257 | >1 E14 | ohm/sq |
| 热性能 | UL文件号, 美国 | | | E121562 | |
| V-0 额定值(测试厚度) | | UL 94 | 0.060 | inch |
| HDT（热畸变温度）, 264 psi, 0.250",未退火 | | ASTM D-648 | 211 | deg F |
| 维卡软化温度, B级 | | ASTM D-1525 | 264 | deg F |
| 热指数, 机械冲击性能 | | UL 746B | 80 | deg C |
| 热指数, 非机械冲击性能 | | UL 746B | 95 | deg C |
| 热指数, 电性能 | | UL 746B | 95 | deg C |
| 5VA 额定值(测试厚度) | | UL 94 | 0.120 | inch |
| HDT（热畸变温度）, 66 psi, 0.250", 未退火 | | ASTM D-648 | 229 | deg F |