Rheological Properties
Melt Volume Rate 220 °C/10 kg	ISO 1133	cm³/10 min	24
Mechanical Properties
Izod Notched Impact Strength, 23 °C	ISO 180/A	kJ/m2	2.5
Charpy Notched Impact Strength, 23° C	ISO 179	kJ/m²	1.5
Charpy Unnotched, 23° C	ISO 179	kJ/m²	12
Izod Unnotched Impact Strength	ISO 180	kJ/m2	12
Tensile Stress at Yield, 23° C	ISO 527	MPa	60
Tensile Modulus	ISO 527	MPa	3300
Nominal Strain at Break, 23 °C	ISO 527	%	2.5
Flexural Strength	ISO 178	MPa	100
Flexural Modulus	ISO 178	MPa	3400
Hardness, Rockwell		M scale	70
Hardness, Ball Indentation	ISO 2039-1	MPa	168
Thermal Properties
Vicat Softening Temperature VST/B/50 (50°C/h, 50N)	ISO 306	°C	98
Vicat Softening Temperature, B/1 (120°C/h, 10N)	ASTM D 1525	°C	105
Heat Distortion Temperature, B (0.45 MPa)	ISO 75	°C	90
Heat Deflection Temperature A; (annealed, 1.8 MPa)	ISO 75	°C	80
Optical Properties
Refractive Index, Sodium D Line	ISO 489	-	1.57
Light Transmission at 550 nm	ASTM D 1003	%	91.3
Haze	ASTM D 1003	%	0.3
Other Properties
Density	ISO 1183	kg/m3	1080
Moisture Absorption, Equilibrium 23°C/50% RH	ISO 62	%	0.10
Processing
Linear Mold Shrinkage	ISO 294-4	%	0.2 to 0.6
Melt Temperature Range	ISO 294	°C	200 - 240
Mold Temperature Range	ISO 294	°C	30 - 60
Rear Temperature Range		°C	180 - 210
Middle Temperature Range		°C	200 - 230
Front Temperature Range		°C	210 - 240
Injection Velocity	ISO 294	mm/s	Slow to Moderate
Drying Temperature		°C	80
Drying Time		h	2
Max Service Temperature		°C	260