一. product features:
1, molding temperature is low, vulcanization  speed is good, can improve the production efficiency.
2, don't need to   vulcanize secondly  .After molding, product tasteless, non-toxic, can comply with FDA standards (not adding other additives).
3, Can improve  anti- yellow  and transparency of  products,

二. Methods and sequence of adding  curing agent  :
1,  mixing silica gel in the mixing machine evenly, add LTC - A after surface smooth.
2, after LTC - A is full, join the LTC - B to  mix.
3, fully mixing evenly after discharging.
Three, standard addition amount and molding conditions:
Silica gel of 100 (mass ratio) : LTC - A 0.5 to 0.8 (quality)/LTC - 2 B, add concrete proportion and performance of rubber ingredients \ \ products \ molding conditions on size, please pay attention to adjust

铂金低温硫化剂LTC-A/B

本硫化剂有效成分为铂金络合物，具有硫化温度低、卫生级别高、产品无味、透明性好、物理性能好等特点。

一、 产品特性：

1、 成型温度低，加硫速度快，可提高生产效率。

2、 不需要做二次加硫，成型后产品无味、无毒，可符合FDA标准（不添加其他添加剂）。

3、 可提高成型品抗黄性及透明性。

二、 加硫剂添加方法及顺序：

1、 先将硅胶在开炼机上混炼均匀，待表面平滑后添加LTC-A.

2、 将LTC-A充分后,加入LTC-B进行混炼.

3、 完全混炼均匀后即可出料。

三、 标准添加量及成型条件：

       硅胶 100份(质量比) ：LTC-A 0.5-0.8(质量份)/LTC-B 2份， 具体添加比例和胶料性能\成分\制品大小\成型条件有关,请注意调整 

四、 注意事项：

1、 所使用硅胶请确认为适合使用铂金催化剂硅胶品种。

2、 尽量控制炼胶机温度(<40度)，避免高温下操作，温度过高会导致胶料提早交联固化，最好需要有冷却水做循环冷却。

3、 LTC-A与LTC-B绝对不能互相混合，一经混合会立即硫化，产生硬块。

4、 硫化剂需储存于阴凉场所，最好在低温下(<摄氏5度)分开存放，使用完容器需紧密盖好。

5、 硫化剂避免用金属器皿取料，因为静电有可能导致危险，最好用木制或直接用手戴手套取料。取A/B成份且勿使用同一工具,防止混合.

 6、 胶料混炼完出料后需尽早(8-12小时内)使用完毕(具体保存时间和硫化剂添加比例\温度及硅胶成分有很大关系)。

7、 不同产品以及不同成型条件需调整添加比例，但不同添加比例会影响其存放时间、加硫速度以及物性。