3.1Ingredients: Mixing pasteof silicone anti- yellow agent and rubber. Density20 ℃ :0.95g/cm3
flashpoint:18 ℃
3.2 use ratio: 1.2%- 1.5%.
3.3 this product is very volatile, so after adding it , should use the film to cover, completely . So,Please run out within 24 hours, otherwise it vulcanizstion become slow maybe . So that u need add more .
3.4 the volatile may also be due to the silicone electrostatic accumulation .It will cause fire , so add curing agent strictly to prevent electrostatic accumulation. Methods are:
3.5 this product used in silica gel has a certain resistance to yellow.4
Purpose:The effective constituent of vulcanizing agent C18 is a bifunctional peroxide. it can be used as a crosslinking of natural or synthetic rubber , and can also be used as the crosslinking of thermoplastic polyolefin
特性：本硫化剂的有效成分为容易挥发的过氧化物, 为乙烯基专用硅胶高温硫化剂。所生产的硅橡胶制品与用普通双二五相比：更加适合厚制品，由于其分解物气味低，更适合生产食品级要求或要求气味低的产品。其抗黄性膏状产品C-18，操作性好，抗黄性好，易分散和称量。
2 典型应用：本品可用于甲基乙烯基硅橡胶的交联剂。典型交联温度：165-195℃（硫变仪t90约120-140秒）
3 产品说明（膏状）与使用：
3.1 成份：硅胶抗黄剂和硅生胶混合膏体。密度20℃：0.95g/cm3 闪点：18℃
3.2 使用比例：1.2%-1.5%，具体添加比例和硅胶类型/加硫均匀度/硫化工艺等有很大关系。
3.3 本品具有很大的挥发性，因此加硫后，应使用薄膜完全覆盖，并建议在24小时内用完，否则可能发生硫化速度变慢现象，此时需要补加本品。
3.4 其挥发性也可能由于硅胶静电累积导致起火，因此加硫时要严格防止静电累积。方法有：
3.5 本品在于硅胶中使用具有一定抗黄性。
4 用途：硫化剂C18中的有效成份是一个双官能团的过氧化物，它可以用作天然或者合成橡胶的交联，同样也可以用作热塑性聚烯烃的交联。
5 产品规格：
外观：透明均匀的膏体含量：34-36%
6 热稳定性：
本品对热/紫外线极不稳定，可产生放热自加速分解。主要分解物：丙酮，甲烷，叔戊醇，叔丁醇，乙烷等
7 包装和运输：
7.1 标准的包装是20L塑料桶装19公斤过氧化物产品。
7.2 包装和运输符合国际法规。关于其他规格包装的可用性，请联系彩源公司销售代表。
7.3 C18纯品属E类有机过氧化物；膏状固体；级别5.2；UN3107。
8 储存：
8.1 保持容器密闭。推荐有最高储存温度（TSmax）<15℃.
8.2 当按照所推荐的条件贮存时，C18在交付后至少可在6个月内保持产品规格范围内。
8.3 在干燥、通风良好的场所贮存、远离热源和点火源、避免阳光直晒。
8.4 禁止在贮藏室称量分装。避免接触还原剂（如胺）、酸、碱和重金属化合物（如促进剂、干燥剂和金属皂）
8.5 更多关于C18的安全储存、使用与操作的进一步信息，请参考安全数据单（MSDS），在接受该产品前，应全面了解这些信息。